Physical Properties | Metric | English | Comments |
---|---|---|---|
Particle Size | 53 - 106 µm | 53 - 106 µm | Range |
Potters Industries Spheriglass® 2429 Solid Glass Spheres Description: Spheriglass® fine solid glass spheres are used as an additive for thermoplastic and thermosetting resin systems. Glass spheres give products many benefits such as:Low Uniform Shrinkage.. |
|||
Particle Size | <= 53 µm | <= 53 µm | 98% finer |
Malvern Minerals Novacite® 325 Untreated Lamellar Quartz Filler/Extender Novacite® quartz silica has closely controlled sizing that is used extensively in the coatings field. Novacite® has broad acceptance as silica in special purpose, product finishes OEM, automo.. |
|||
Particle Size | <= 53 µm | <= 53 µm | 98% finer |
Malvern Minerals Novakup® 325 Surface-Treated Lamellar Quartz Filler/Extender Novakup® is a surface modified or silane treated Novacite®. It has been used its barrier prosperities in chemical and corrosion resistant applications and as a filler/extender/reinforcing agen.. |
|||
Particle Size | 53 µm | 53 µm | Finer than |
Inhance Fluoro-Seal INHANCE® HD-1800 HDPE Product Description: INHANCE HD-1000 Series Polyethylene Particles are surface-activated High Density Polyethylene (HDPE) in particle or powder form. Surface activation makes the particles easy to.. |
|||
Particle Size | 53 µm | 53 µm | Average Size |
Inhance Fluoro-Seal INHANCE® UH-1250 Ultra High Molecular Weight Polyethylene Product Description: INHANCE UH-1000 series particles are surface-activated Ultra High Molecular Weight Polyethylene (UHMWPE) in powder form. Surface activation makes the particles easy to disperse.. |
|||
Particle Size | 53 - 62 µm | 53 - 62 µm | 90% |
H.C. Starck Amperit® 110.2 Agglomerated Sintered (Mo-Mo2C) |
|||
Particle Size | 53 µm | 53 µm | Maximum of 10% greater than, (NiSF RC 60) |
H.C. Starck Amperit® 119.075 Molybdenum-Nickel SF RC 60 75-25 (Mo / NiSF) Composition is of NiSF RC 60 only |
|||
Particle Size | 53 - 63 µm | 53 - 63 µm | 90% |
H.C. Starck Amperit® 512.074 Agglomerated Sintered Tungsten Carbide - Cobalt (WC-Co) 88-12 |
|||
Particle Size | 53 - 63 µm | 53 - 63 µm | 90% |
H.C. Starck Amperit® 519.074 Agglomerated, Sintered Tungsten Carbide-Cobalt 88-12 (WC-CO) |
|||
Particle Size | 53 - 63 µm | 53 - 63 µm | 90% |
H.C. Starck Amperit® 527.074 Agglomerated, Sintered Tungsten Carbide-Cobalt (WC-Co) 83-17 |
|||
Particle Size | 53 µm | 53 µm | Maximum 10% greater than, for Ni-SF RC 60 |
H.C. Starck Amperit® 560.062 Tungsten Carbide-Cobalt(83-17)-Nickel-SF RC 60 50-50 (Wc-Co / NiSF RC 60) Composition is of NiSF RC 60 only |
|||
Particle Size | 53 µm | 53 µm | Maximum 10% greater than, for Ni-SF RC 60 |
H.C. Starck Amperit® 560.077 Tungsten Carbide-Cobalt(83-17)-Nickel-SF RC 60 50-50 (Wc-Co / NiSF RC 60) Composition is of NiSF RC 60 only |
|||
Particle Size | 53 µm | 53 µm | Maximum of 5% greater than, Ni-SF RC 60 |
H.C. Starck Amperit® 568.062 Tungsten Carbide-Nickel 92-8 - Nickel SF RC 60 65-35 Composition is of NiSF RC 60 only |
|||
Particle Size | 53 - 62 µm | 53 - 62 µm | 90% |
H.C. Starck Amperit® 583.054 Chromium Carbide-Nickel 83-17 (Cr3C2-Ni) |
|||
Particle Size | 53 - 63 µm | 53 - 63 µm | 90% |
H.C. Starck Amperit® 827.054 Zirconium Oxide-Yttrium Oxide 93-7 (ZrO2-Y2O3) |
|||
Particle Size | 53 µm | 53 µm | Maximum of 5% less than |
H.C. Starck Amperweld® AISI 316 L 150/53 µm for Plasma Transferred Arc Surfacing AISI 316 L is a type of low carbon austenitic Cr-Ni-Mo stainless steel with good oxidation resistance in intermittent service to 870°C and in continuous service to 925°C, resistance to intercr.. |
|||
Particle Size | 53 - 63 µm | 53 - 63 µm | 90% |
H.C. Starck Amperit® 558.074 Tungsten Carbide-Cobalt-Chromium 86-10-4 (WC-Co-Cr) |
|||
Particle Size | 53 - 62 µm | 53 - 62 µm | 90% |
H.C. Starck Amperit® 599.074 Agglomerated Sintered Molybdenum Carbide (Cr2O3) |
|||
Particle Size | 53 µm | 53 µm | TEC QSD |
Trelleborg AEM Eccospheres® SID-120Z Sodium Borosilicate Glass Microspheres Eccospheres® glass microspheres are hollow thin-walled glass microspheres composed of sodium borosilicate glass. To the naked eye they resemble a fine, white, free-flowing powder. However, magnific.. |
|||
Particle Size | 53 µm | 53 µm | Maximum of 5% less than |
H.C. Starck Amperit® 415.079 CoNiCrAlY (MCrAlY) |
|||
Particle Size | 53 µm | 53 µm | Maximum of 10% greater than |
H.C. Starck Amperit® 335.066 Nickel Self-fluxing Alloy HRC 60 (NiCrBSi) |
|||
Particle Size | 53 - 63 µm | 53 - 63 µm | 90% |
H.C. Starck Amperit® 529.074 Tungsten Carbide - Hastalloy C 85-15 (NiMoCrFeCo) |
|||
Particle Size | 53 - 63 µm | 53 - 63 µm | 90% |
H.C. Starck Amperit® 547.059 Tungsten Carbide-Nickel 88-12 (WC-Ni) |
|||
Particle Size | 53 - 63 µm | 53 - 63 µm | 90% |
H.C. Starck Amperit® 551.074 Tungsten Carbide - Chromium Carbide - Nickel 70-20-7 (W-CrC-Ni) |