Zhejiang Juner PA-A6-6H High CTI Value Halogen-Free Environmental Protection Flame-Resistant and Reinforced Polyamide
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Mineral Reinforced, Impact Grade |
| Manufacturer | Zhejiang Juner New Materials Co. |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Zhejiang Juner PA-A6-6H High CTI Value Halogen-Free Environmental Protection Flame-Resistant and Reinforced Polyamide.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Circuit Breaker, BaseInformation provided by Zhejiang Juner New Materials Co, Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.55 g/cc | 0.0560 lb/in³ | GB/1033 |
| Water Absorption | 0.60 % | 0.60 % | 23°C•24h |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 60.0 MPa | 8700 psi | GB/1040 |
| Elongation at Break | 2.0 % | 2.0 % | GB/1040 |
| Flexural Strength | 100 MPa | 14500 psi | GB/9341 |
| Flexural Modulus | 8.80 GPa | 1280 ksi | GB/9341 |
| Charpy Impact Unnotched | 2.00 J/cm² | 9.52 ft-lb/in² | IS0179-1:2000 |
| Charpy Impact, Notched | 0.500 J/cm² | 2.38 ft-lb/in² | IS0179-1:2000 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 150 °C | 302 °F | GB1634 |
| Flammability, UL94 | V-0 | V-0 | GB/T2408 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | GB/1410 |
| Comparative Tracking Index | 550 V | 550 V | GB/4207 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 225 - 250 °C | 437 - 482 °F | |
| Mold Temperature | 60.0 - 90.0 °C | 140 - 194 °F | |
| Drying Temperature | 110 °C @Time 18000 sec |
230 °F @Time 5.00 hour |
Chute Hot-Wind |
| 110 °C @Time 18000 sec |
230 °F @Time 5.00 hour |
Horizontal Oven | |
| 110 °C @Time 7200 sec |
230 °F @Time 2.00 hour |
Vacuum Pressure, -0.08 MPa | |
| Injection Pressure | 80.0 - 100 MPa | 11600 - 14500 psi |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Speed of Shoot, % | 35-80 |
Users viewing this material also viewed the following:
- KB Alloys 8% Bismuth Aluminum Alloy
- Momentive Performance Materials RTV102 White Adhesive Sealant, High Strength Paste
- SolVin 367NK Polyvinyl Chloride Medium Viscosity Paste
- Westlake LF1040 Butene Linear Low Density Polyethylene
- A. Schulman POLYBATCH™ Navajo 10275U/4 Concentrate Based In LDPE
- Ashley Polymers Ashlene® 630-33GU Nylon 6, 33% Glass Reinforced
- BNZ Materials Bazelite 2600 LI Insulating Castable
- Parker Chomerics Tecknit SC-Consil® 861 Carbon-Filled Silicone Elastomer
Copyright © lookpolymers.com All Rights Reserved