Westlake Elevate™ DA528AA 18.5% Ethylene Vinyl Acetate Copolymer

Category	Polymer , Thermoplastic , Ethylene Vinyl Acetate
Manufacturer	Westlake Chemical Corporation
Trade Name	Elevate™
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Westlake Elevate™ DA528AA 18.5% Ethylene Vinyl Acetate Copolymer.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Westlake ELEVATE™ DA528 is an ethylene vinyl acetate copolymer with 18.5% VA. DA528 is designed for blown and cast films requiring excellent optics and low heat seal initiation. High melt strength makes DA528 an excellent choice for profile extrusions, molding, and foaming applications requiring high VA content.Application/UsesFlexible packaging filmsPeelable seals, adhesive layersInjection and blow moldingHot melt adhesives and blendsProfile extrusions, tubing, wire & cableFDA: This material complies with FDA regulations in 21 CFR, section 177.1350.All information provided by Westlake Chemical

Physical Properties	Metric	English	Comments
Density	0.940 g/cc	0.0340 lb/in³	ASTM D1505
Vinyl Acetate Content	18.5 %	18.5 %
Thickness	38.1 microns	1.50 mil	Thickness tested
Melt Flow	2.5 g/10 min	2.5 g/10 min	ASTM D1238

Mechanical Properties	Metric	English	Comments
Dart Drop	10.2 g/micron	260 g/mil	ASTM D1709
Dart Drop Test	390 g	0.860 lb	ASTM D1709
Film Tensile Strength at Break, MD	24.8 MPa	3600 psi	ASTM D638
Film Tensile Strength at Break, TD	24.1 MPa	3500 psi	ASTM D638
1% Secant Modulus, MD	42.1 MPa	6100 psi	ASTM D882
1% Secant Modulus, TD	50.3 MPa	7300 psi	ASTM D882

Thermal Properties	Metric	English	Comments
Melting Point	85.0 °C	185 °F	DSC Peak; ASTM D3418

Optical Properties	Metric	English	Comments
Haze	3.5 %	3.5 %	ASTM D1003
Gloss	82 %	82 %	at 45º; ASTM D2457

Processing Properties	Metric	English	Comments
Melt Temperature	<= 193 °C	<= 379 °F	Blown Film
	<= 210 °C	<= 410 °F	Cast Film
Blow-up Ratio (BUR)	2.5	2.5

Descriptive Properties	Value	Comments
Process	Film

Users viewing this material also viewed the following: