- Wellman Wellamid® GF33-66/6 XE-WBK 33% Glass Fiber Reinforced, Weatherable Black Nylon 66/6
Wellman Wellamid® GF33-66/6 XE-WBK 33% Glass Fiber Reinforced, Weatherable Black Nylon 66/6
| Category | Polymer , Thermoplastic , Nylon , Nylon 6/66 , Nylon 66/6, 30% Glass Fiber Reinforced |
| Manufacturer | Wellman Engineering Resins |
| Trade Name | Wellamid® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Wellman Wellamid® GF33-66/6 XE-WBK 33% Glass Fiber Reinforced, Weatherable Black Nylon 66/6.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Glass Fiber Reinforced, Weatherable Black Nylon 66/6Information provided by Wellman.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.39 g/cc | 0.0502 lb/in³ | ISO 1183-87 |
| Filler Content | 33 % | 33 % | |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm | 0.0010 - 0.0030 in/in | ISO DIS 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0070 - 0.011 cm/cm | 0.0070 - 0.011 in/in | ISO DIS 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 155 MPa | 22500 psi | ISO 527-93 |
| Elongation at Break | 3.0 % | 3.0 % | ISO 527-93 |
| Flexural Strength | 240 MPa | 34800 psi | ISO 178-93 |
| Flexural Modulus | 8.60 GPa | 1250 ksi | ISO 178-93 |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² | 4.76 ft-lb/in² | ISO 180-93 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 260 °C | 500 °F | ISO 3146 |
| Deflection Temperature at 1.8 MPa (264 psi) | 220 °C | 428 °F | ISO 75-93 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Cycolac® MG94U ABS
- Solvay Specialty Polymers Solef® 6012 Polyvinylidene Fluoride (PVDF) (Unverified Data**)
- Solvay GERONOL® RE/70 Surfactant
- Polyram BondyRam® 6000 Maleic Anhydride grafted Acrylonitrile-Butadiene-Styrene coupling agent
- Goodfellow Carbon-Carbon Composite
- Hexcel® Redux® 208/5-NA Foaming adhesive film
- A. Schulman SCHULAMID® 66 MK4015H 40% Glass Fiber/Mineral Reinforced, Heat Stabilized Nylon 66
- AK Steel Cold Rolled Carbon Steel, Extra Deep Drawing Steel (EDDS), Standard Grade
- Beijing Chemical Industry KAIFA® 302-G30 PBT Resin
- 3M 7942 Aluminum Foil Label Material
Copyright © lookpolymers.com All Rights Reserved