- Lehmann & Voss LUVOCOM® 1104-7598 Polyether ketone, with carbon fiber, PTFE, lubricant modified
Lehmann & Voss LUVOCOM® 1104-7598 Polyether ketone, with carbon fiber, PTFE, lubricant modified
| Category | Polymer , Thermoplastic , Polyketone |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 1104-7598 Polyether ketone, with carbon fiber, PTFE, lubricant modified.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Automotive industry, mechanical- and precision engineering.Improved strength and stiffnes at elevated temperatures.Improved fatigue properties.Thermic, mechanic and chemical highly stressed parts.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.45 g/cc | 1.45 g/cc | ISO 1183 |
| Water Absorption | <= 0.10 % | <= 0.10 % | 23°C/24h |
| Linear Mold Shrinkage | 0.0030 - 0.0060 cm/cm | 0.0030 - 0.0060 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 158 MPa | 22900 psi | |
| Elongation at Yield | 1.8 % | 1.8 % | |
| 2.4 % | 2.4 % | flexural | |
| Modulus of Elasticity | 14.0 GPa | 2030 ksi | |
| Flexural Strength | 225 MPa | 32600 psi | |
| Flexural Modulus | 12.0 GPa | 1740 ksi | |
| Charpy Impact Unnotched | 3.30 J/cm² | 15.7 ft-lb/in² | edgewise; ISO 179 1eU |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 260 °C | 500 °F | |
| 290 °C | 554 °F | short term | |
| Vicat Softening Point | >= 325 °C | >= 617 °F | DIN ISO 306 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Insulation Resistance | <= 100000 ohm | <= 100000 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 390 °C | 734 °F | mass temp |
| Nozzle Temperature | 390 - 420 °C | 734 - 788 °F | |
| Zone 1 | 370 - 390 °C | 698 - 734 °F | |
| Zone 2 | 380 - 420 °C | 716 - 788 °F | |
| Zone 3 | 390 - 420 °C | 734 - 788 °F | |
| Mold Temperature | 180 - 230 °C | 356 - 446 °F | |
| Drying Temperature | 140 °C @Time 14400 - 57600 sec |
284 °F @Time 4.00 - 16.0 hour |
Dehumidifying dryer |
| 150 °C @Time 14400 - 28800 sec |
302 °F @Time 4.00 - 8.00 hour |
Air-Circulation Dryer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | natural color (black) |
Users viewing this material also viewed the following:
- Pyrotek G-1 Low-Temperature Felt
- LG Chemical LUTENE FB0800 LDPE Blown Film
- SABIC Innovative Plastics NORYL WCD933 PPE-TPE
- Unitika elitel UE3215 Polyester, Pellet
- CP-Polymer-Technik Wellamid® 6000 MR 309 HWCP Mineral Nylon 6, Heat Stabilized, Conditioned
- DuPont Performance Polymers Delrin® 988PA NC010 Acetal (POM)
- Chosun Refractories CTC-65SH Monolithic Refractories for Ladle and Tundish
- Akzo Nobel Expancel® 551 WU 80 Wet unexpanded microspheres
- Arlon 44570R025 0.025" (0.635 mm) Uncured Silicone Rubber with Fiberglass Substrate
- Lehmann & Voss LUVOCOM® 1301-0824 PPS, linear, with carbon fiber
Copyright © lookpolymers.com All Rights Reserved