Covestro Apec® DP9-9354T High-Heat Polycarbonate, Transparent, Flame-Retardant  (discontinued **)

Category	Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Unreinforced, Flame Retardant
Manufacturer
Trade Name
Port	Ningbo port,China
Trade Terms	EXW, FOB, CFR, CIF
Payment Terms	L/C, T/T, PayPal
Download PDF	Covestro Apec® DP9-9354T High-Heat Polycarbonate, Transparent, Flame-Retardant  (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

Information provided by Bayer Corporation, Plastics DivisionAs of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and has officially adopted its new name – Covestro. This product was discontinued prior to the separation.

Physical Properties	Metric	English	Comments
Density	1.15 g/cc	0.0415 lb/in³	ASTM D792
Water Absorption	0.20 %	0.20 %	24 hour immersion; ASTM D570
Linear Mold Shrinkage	0.0080 - 0.0090 cm/cm	0.0080 - 0.0090 in/in	ASTM D955
Melt Flow	8.0 g/10 min <br>@Load 2.16 kg,<br> Temperature 330 °C	8.0 g/10 min <br>@Load 4.76 lb,<br> Temperature 626 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	62.0 MPa	8990 psi	ASTM D638
Tensile Strength, Yield	66.0 MPa	9570 psi	ASTM D638
Elongation at Break	50 %	50 %	ASTM D638
Elongation at Yield	6.0 %	6.0 %	ASTM D638
Tensile Modulus	2.20 GPa	319 ksi	ASTM D638
Flexural Yield Strength	86.0 MPa	12500 psi	ASTM D790
Flexural Modulus	2.28 GPa	331 ksi	ASTM D790
Izod Impact, Notched	1.00 J/cm <br>@Thickness 3.17 mm	1.87 ft-lb/in <br>@Thickness 0.125 in	ASTM D256
Izod Impact, Unnotched	NB	NB	ASTM D256
	NB <br>@Temperature -40.0 °C	NB <br>@Temperature -40.0 °F	ASTM D256
Impact Test	58.0 J <br>@Thickness 3.20 mm	42.8 ft-lb <br>@Thickness 0.126 in	Instrumented Impact, Total Energy; 3.2 mm thick, 15 mph, 3 in. clamp, 0.5 in. dart; ASTM D3763

Thermal Properties	Metric	English	Comments
CTE, linear	70.0 µm/m-°C <br>@Temperature 20.0 °C	38.9 µin/in-°F <br>@Temperature 68.0 °F	ASTM D696
Thermal Conductivity	0.210 W/m-K	1.46 BTU-in/hr-ft²-°F	ASTM C177
Deflection Temperature at 0.46 MPa (66 psi)	174 °C <br>@Thickness 3.20 mm	345 °F <br>@Thickness 0.126 in	ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	162 °C <br>@Thickness 3.17 mm	324 °F <br>@Thickness 0.125 in	ASTM D648
Vicat Softening Point	185 °C	365 °F	Rate B; ASTM D1525
Flammability, UL94	V-0 <br>@Thickness 3.00 mm	V-0 <br>@Thickness 0.118 in
	V-0 <br>@Thickness 3.00 mm	V-0 <br>@Thickness 0.118 in
Oxygen Index	35 %	35 %	ASTM D2863

Optical Properties	Metric	English	Comments
Refractive Index	1.573	1.573	ASTM D542
Haze	2.0 % <br>@Thickness 3.17 mm	2.0 % <br>@Thickness 0.125 in	ASTM D1003
Transmission, Visible	87 % <br>@Thickness 3.20 mm	87 % <br>@Thickness 0.126 in	ASTM D1003

Electrical Properties	Metric	English	Comments
Electrical Resistivity	>= 1.00e+16 ohm-cm	>= 1.00e+16 ohm-cm	ASTM D257
Surface Resistance	>= 1.00e+16 ohm	>= 1.00e+16 ohm	ASTM D257
Dielectric Constant	2.9 <br>@Frequency 60 Hz	2.9 <br>@Frequency 60 Hz	ASTM D150
	2.9 <br>@Frequency 1e+6 Hz	2.9 <br>@Frequency 1e+6 Hz	ASTM D150
Dielectric Strength	>= 16.0 kV/mm <br>@Thickness 3.17 mm	>= 406 kV/in <br>@Thickness 0.125 in	ASTM D149
Dissipation Factor	0.0010 <br>@Frequency 60 Hz	0.0010 <br>@Frequency 60 Hz	ASTM D150
	0.010 <br>@Frequency 1e+6 Hz	0.010 <br>@Frequency 1e+6 Hz	ASTM D150
Arc Resistance	60 - 120 sec <br>@Thickness 3.00 mm	60 - 120 sec <br>@Thickness 0.118 in	UL Rating PLC 6 (60-120 sec)
Comparative Tracking Index	>= 600 V <br>@Thickness 3.00 mm	>= 600 V <br>@Thickness 0.118 in	UL Rating PLC 0 (>600 V)
Hot Wire Ignition, HWI	30 - 60 sec <br>@Thickness 1.50 mm	30 - 60 sec <br>@Thickness 0.0591 in	UL Rating PLC 2 (30-60 sec)
High Amp Arc Ignition, HAI	>= 120 arcs <br>@Thickness 1.50 mm	>= 120 arcs <br>@Thickness 0.0591 in	UL Rating PLC 0 (>120 arcs)
High Voltage Arc-Tracking Rate, HVTR	25.4 - 80.0 mm/min <br>@Thickness 3.00 mm	1.00 - 3.15 in/min <br>@Thickness 0.118 in	UL Rating PLC 2 (25.4-80 mm/min.)

Users viewing this material also viewed the following:

Covestro Apec® DP9-9354T High-Heat Polycarbonate, Transparent, Flame-Retardant &nbsp;(discontinued **)

Covestro Apec® DP9-9354T High-Heat Polycarbonate, Transparent, Flame-Retardant (discontinued **)