Victrex® PEEK 450FC30 General Purpose
| Category | Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK) , Polyetheretherketone, PEEK, Carbon Fiber Filled |
| Manufacturer | Victrex |
| Trade Name | PEEK |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Victrex® PEEK 450FC30 General Purpose.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Product Description: High performance thermoplastic material, 30% reinforced with carbon fibre / graphite / PTFE PolyEtherEtherKetone (PEEK), semi crystalline, granules for injection molding and extrusion, standard flow, FDA food contact compliant, color black.Typical Application Areas: Tribological applications for high strength. Excellent wear resistance, very low coefficient of friction, low coefficient of thermal expansion. Chemically resistant to aggressive environmentsInformation provided by Victrex.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.45 g/cc | 0.0524 lb/in³ | ISO 1183 |
| Water Absorption at Saturation | 0.35 % @Temperature 23.0 °C |
0.35 % @Temperature 73.4 °F |
immersion; ISO 62-1 |
| 0.35 % @Temperature 100 °C |
0.35 % @Temperature 212 °F |
immersion; ISO 62-1 | |
| Viscosity | 550000 cP @Temperature 400 °C |
550000 cP @Temperature 752 °F |
melt; ISO 11443 |
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | 385°C nozzle, 200°C tool; ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0070 cm/cm | 0.0070 in/in | 385°C nozzle, 200°C tool; ISO 294-4 |
| Spiral Flow | 8.00 cm @Thickness 1.00 mm |
3.15 in @Thickness 0.0394 in |
385°C nozzle, 200°C tool |
| 38.0 cm @Thickness 3.00 mm |
15.0 in @Thickness 0.118 in |
385°C nozzle, 200°C tool |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 83 | 83 | ISO 868 |
| Tensile Strength at Break | 35.0 MPa @Temperature 275 °C |
5080 psi @Temperature 527 °F |
ISO 527 |
| 45.0 MPa @Temperature 225 °C |
6530 psi @Temperature 437 °F |
ISO 527 | |
| 55.0 MPa @Temperature 175 °C |
7980 psi @Temperature 347 °F |
ISO 527 | |
| 95.0 MPa @Temperature 125 °C |
13800 psi @Temperature 257 °F |
ISO 527 | |
| 150 MPa @Temperature 23.0 °C |
21800 psi @Temperature 73.4 °F |
ISO 527 | |
| Elongation at Break | 2.3 % | 2.3 % | ISO 527 |
| Tensile Modulus | 13.0 GPa | 1890 ksi | ISO 527 |
| Flexural Strength | 45.0 MPa @Temperature 275 °C |
6530 psi @Temperature 527 °F |
ISO 178 |
| 80.0 MPa @Temperature 175 °C |
11600 psi @Temperature 347 °F |
ISO 178 | |
| 160 MPa @Temperature 125 °C |
23200 psi @Temperature 257 °F |
ISO 178 | |
| 230 MPa @Temperature 23.0 °C |
33400 psi @Temperature 73.4 °F |
ISO 178 | |
| Flexural Modulus | 11.5 GPa | 1670 ksi | ISO 178 |
| Compressive Strength | 45.0 MPa @Temperature 200 °C |
6530 psi @Temperature 392 °F |
ISO 604 |
| 110 MPa @Temperature 120 °C |
16000 psi @Temperature 248 °F |
ISO 604 | |
| 170 MPa @Temperature 23.0 °C |
24700 psi @Temperature 73.4 °F |
ISO 604 | |
| Izod Impact, Notched (ISO) | 7.00 kJ/m² @Temperature 23.0 °C |
3.33 ft-lb/in² @Temperature 73.4 °F |
ISO 180/A |
| Izod Impact, Unnotched (ISO) | 35.0 kJ/m² @Temperature 23.0 °C |
16.7 ft-lb/in² @Temperature 73.4 °F |
ISO 180/U |
| Charpy Impact Unnotched | 3.50 J/cm² @Temperature 23.0 °C |
16.7 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1U |
| Charpy Impact, Notched | 0.500 J/cm² @Temperature 23.0 °C |
2.38 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 45.0 µm/m-°C @Temperature <=143 °C |
25.0 µin/in-°F @Temperature <=289 °F |
Average below Tg; ISO 11359 |
| 115 µm/m-°C @Temperature >=143 °C |
63.9 µin/in-°F @Temperature >=289 °F |
Average above Tg; ISO 11359 | |
| CTE, linear, Parallel to Flow | 15.0 µm/m-°C @Temperature <=143 °C |
8.33 µin/in-°F @Temperature <=289 °F |
Below Tg; ISO 11359 |
| 20.0 µm/m-°C @Temperature >=143 °C |
11.1 µin/in-°F @Temperature >=289 °F |
Above Tg; ISO 11359 | |
| Thermal Conductivity | 0.850 W/m-K | 5.90 BTU-in/hr-ft²-°F | Average; ISO 22007-4 |
| 1.70 W/m-K | 11.8 BTU-in/hr-ft²-°F | Along flow; ISO 22007-4 | |
| Melting Point | 343 °C | 649 °F | ISO 11357 |
| Deflection Temperature at 1.8 MPa (264 psi) | 315 °C | 599 °F | ISO 75-f |
| Glass Transition Temp, Tg | 143 °C | 289 °F | Onset; ISO 11357 |
| 150 °C | 302 °F | Midpoint; ISO 11357 | |
| UL RTI, Mechanical with Impact | 180 °C | 356 °F | UL 746B |
| UL RTI, Mechanical without Impact | 240 °C | 464 °F | UL 746B |
| Oxygen Index | 43 % | 43 % | ISO 4289 |
| Glow Wire Test | 960 °C @Thickness 2.00 mm |
1760 °F @Thickness 0.0787 in |
IEC 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+10 ohm-cm | 1.00e+10 ohm-cm | IEC 60093 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | <= 100 °C | <= 212 °F | Hopper Temperature |
| Nozzle Temperature | 385 °C | 725 °F | |
| Mold Temperature | 170 - 200 °C | 338 - 392 °F | |
| Dry Time | 3.00 hour @Temperature 150 °C |
3.00 hour @Temperature 302 °F |
|
| 5.00 hour @Temperature 120 °C |
5.00 hour @Temperature 248 °F |
Users viewing this material also viewed the following:
- S&E Specialty Polymers TufFlex™ GTPE-2272SG-K8 TPE Compound
- Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 1.0 mm thick sheet
- Kuraray Vectran® UM 1500/300 LCP Fiber
- Momentive Performance Materials Siloprenâ„¢ LSR TOPCOAT HE Liquid Silicone Rubber Specialty Coating
- Karina 828-08/20-AY-ERYB-PO Beige PVC Compound
- Solvay TECHNYL® A 218W V15 PA66, 15% glass fiber, Conditioned
- Zylog Hipolyene® 7151 M1 HF Thermoplastic Polyolefin & PP Compound
- Trelleborg E647 EPDM Rubber
- Devcon Plastic Steel® Putty (A) Epoxy
- ConocoPhillips 320 Bearing Oil
Copyright © lookpolymers.com All Rights Reserved