Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Unreinforced |
Manufacturer | Grupo Repol |
Trade Name | Dinalon® |
Port | Shanghai port,China |
Trade Terms | FOB, CFR, CIF |
Payment Terms | L/C, T/T, Western Union |
Download PDF | Grupo Repol Dinalon® A3S25 PA66 Unreinforced.pdf ![]() |
Price | EMAIL US sales@lookpolymers.com |
Physical Properties | Metric | English | Comments |
---|---|---|---|
Density | 1.14 g/cc | 0.0412 lb/in³ | ISO 1183/A |
Moisture Absorption at Equilibrium | <= 0.25 % | <= 0.25 % | Karl-Fischer; ISO 15512/A |
Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 80.0 MPa | 11600 psi | ISO 527 |
Elongation at Yield | 5.0 % | 5.0 % | ISO 527 |
Tensile Modulus | 3.00 GPa | 435 ksi | ISO 527 |
Flexural Strength | 85.0 MPa | 12300 psi | ISO 178 |
Flexural Modulus | 1.70 GPa | 247 ksi | ISO 178 |
Charpy Impact Unnotched | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ISO 179/1eU |
Charpy Impact, Notched | 0.300 J/cm² @Temperature 23.0 °C |
1.43 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
Thermal Properties | Metric | English | Comments |
---|---|---|---|
Deflection Temperature at 1.8 MPa (264 psi) | 65.0 °C | 149 °F | ISO 75/A |
Vicat Softening Point | >= 230 °C | >= 446 °F | 50N; ISO 306 |
Flammability, UL94 | V-2 @Thickness 1.60 mm |
V-2 @Thickness 0.0630 in |