Unitika UG-100-20 Engineering Plastic
| Category | Polymer , Thermoplastic , Polyarylate |
| Manufacturer | Unitika |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Unitika UG-100-20 Engineering Plastic.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Excellent creep resistance, dimensional stability at high temperatureInformation provided by Unitika Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.36 g/cc | 0.0491 lb/in³ | ASTM D792 |
| Water Absorption | 0.24 % @Thickness 3.17 mm, Time 86400 sec |
0.24 % @Thickness 0.125 in, Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0020 cm/cm @Thickness 3.00 mm |
0.0020 in/in @Thickness 0.118 in |
|
| Linear Mold Shrinkage, Transverse | 0.0010 - 0.0020 cm/cm @Thickness 3.00 mm |
0.0010 - 0.0020 in/in @Thickness 0.118 in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 122 | 122 | ASTM D785 |
| Tensile Strength at Break | 99.0 MPa | 14400 psi | ASTM D638 |
| Elongation at Break | 4.5 % | 4.5 % | ASTM D638 |
| Flexural Strength | 157 MPa | 22800 psi | ASTM D790 |
| Flexural Modulus | 2.50 GPa | 363 ksi | ASTM D790 |
| Izod Impact, Notched | 0.490 J/cm @Thickness 3.17 mm |
0.918 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 21.0 µm/m-°C | 11.7 µin/in-°F | ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 180 °C | 356 °F | ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 4.60e+14 ohm-cm | 4.60e+14 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.0 @Frequency 1.00e+6 Hz |
3.0 @Frequency 1.00e+6 Hz |
ASTM D150 |
| Dielectric Strength | 35.0 kV/mm | 889 kV/in | ASTM D149 |
| Dissipation Factor | 0.015 @Frequency 1.00e+6 Hz |
0.015 @Frequency 1.00e+6 Hz |
ASTM D150 |
| Arc Resistance | 120 sec | 120 sec | ASTM D495 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 310 - 330 °C | 590 - 626 °F | |
| Middle Barrel Temperature | 340 - 360 °C | 644 - 680 °F | |
| Front Barrel Temperature | 350 - 370 °C | 662 - 698 °F | |
| Nozzle Temperature | 350 - 370 °C | 662 - 698 °F | |
| Mold Temperature | 120 - 140 °C | 248 - 284 °F | actual surface temp |
| Drying Temperature | 140 °C | 284 °F | |
| Dry Time | 6.00 - 24.0 hour | 6.00 - 24.0 hour | |
| Back Pressure | 0.490 - 1.47 MPa | 71.1 - 213 psi | gage pressure |
Users viewing this material also viewed the following:
- PlastiComp Complet® LCF50 - PA66 Nylon 66, 50% Long Carbon Fiber Reinforced
- Techmer ES HiFill® PA6 0390 BK
- Styron CALIBREâ„¢ 201-06 Polycarbonate
- UBE 5034MT2 Nylon 6/66 Monofilament (Drawing Ratio=4.5)
- ExxonMobil Varsol™ DX 140 Naphtha Non-dearomatized Fluid
- Chosun Refractories ZM-2 Special Mortar
- Alliance S-30A Samarium Cobalt Magnetic Material
- Ashley Polymers Ashlene® P114WO PBT Polyester
- DuPont Performance Polymers Delrin® 100P NC010 Acetal Homopolymer (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved