- Polyram PlusTek PA320G6 Nylon 6.6, 30% Glass Fiber, Flame Retardant
Polyram PlusTek PA320G6 Nylon 6.6, 30% Glass Fiber, Flame Retardant
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Glass Fiber Filled, Flame Retardant |
| Manufacturer | Polyram |
| Trade Name | PlusTek |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polyram PlusTek PA320G6 Nylon 6.6, 30% Glass Fiber, Flame Retardant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
30% glass fiber reinforced, flame retardant polyamide 6.6 for injection molding applicationsInformation provided by Polyram Ram On Ind.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.38 g/cc | 0.0499 lb/in³ | DIN 53479 |
| Water Absorption | 4.5 % | 4.5 % | DIN 53495 |
| Moisture Absorption at Equilibrium | 1.5 % | 1.5 % | 50%RH; DIN 53714 |
| Linear Mold Shrinkage | 0.0030 - 0.0040 cm/cm | 0.0030 - 0.0040 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 122 | 122 | ASTM-D785 |
| Tensile Strength, Yield | 150 MPa | 21800 psi | ASTM-D638 |
| Elongation at Break | 2.0 % | 2.0 % | ASTM-D638 |
| Flexural Strength | 200 MPa | 29000 psi | ASTM D790 |
| Flexural Modulus | 8.00 GPa | 1160 ksi | ASTM-D790 |
| Izod Impact, Notched | 0.600 J/cm @Temperature 23.0 °C |
1.12 ft-lb/in @Temperature 73.4 °F |
ASTM-D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 256 °C | 493 °F | |
| Maximum Service Temperature, Air | 115 °C | 239 °F | Continuous Use |
| >= 200 °C | >= 392 °F | Short peaks operation | |
| Deflection Temperature at 0.46 MPa (66 psi) | 235 °C | 455 °F | DIN 53461 |
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | DIN 53461 |
| Flammability, UL94 | V-0 @Thickness 3.00 mm |
V-0 @Thickness 0.118 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | DIN 53482 |
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | DIN 53482 |
| Dielectric Constant | 3.7 @Frequency 1e+6 Hz |
3.7 @Frequency 1e+6 Hz |
VDE 0303/4 |
| Dielectric Strength | 80.0 kV/mm | 2030 kV/in | VDE 0303/4 |
Users viewing this material also viewed the following:
- LyondellBasell Petrothene® NA345009 Low Density Polyethylene (Film Extrusion)
- Lubrizol ESTANE® T4065 Ester Based Thermoplastic Polyurethane (European Grade)
- Tisan TISLAMID® 66 25% Glass Fiber Reinforced Flame Retardant (V0). Heat Stabilized Nylon 66
- A. Schulman POLYBATCH™ Brown 1281 Concentrate Based In Polyethylene
- China Tungsten NT4 Titanium Carbonitride Alloy
- Esstech X-743-0000 Ethoxylated Bis Phenol A Dimethacrylate, C43H64O14
- ExxonMobil Greasrex K-170
- Axiall 21570 Coax & Telecom Flexible PVC
- Cheng Yu Plastic FV30715 POM, 15% Mineral Reinforced
- Multibase Multi-Flam™ 0106 PP Black Polypropylene
Copyright © lookpolymers.com All Rights Reserved