Special Metals INCOLOY® Alloy 825
| Category | Metal , Nonferrous Metal , Nickel Alloy , Superalloy |
| Manufacturer | Special Metals (includes the former Inco Alloys International Inc.) |
| Trade Name | INCOLOY® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Special Metals INCOLOY® Alloy 825.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
A nickel-iron-chromium alloy with additions of molybdenum and copper. It has excellent resistance to both reducing and oxidizing acids, to stress-corrosion cracking, and to localized attack such as pitting and crevice corrosion. The alloy is especially resistant to sulfuric and phosphoric acids. Used for chemical processing, pollution-control equipment, oil and gas well piping, nuclear fuel reprocessing, acid production, and pickling equipment. Standard product forms are round, flats, forging stock, pipe, tube, plate, sheet, strip, and wire.Data provided by the manufacturer, Special Metals.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 8.14 g/cc | 0.294 lb/in³ |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 690 MPa | 100000 psi | Annealed |
| 590 MPa @Temperature 550 °C |
85600 psi @Temperature 1020 °F |
Annealed prior to test | |
| Tensile Strength, Yield | 310 MPa | 45000 psi | Annealed |
| 220 MPa @Temperature 550 °C |
31900 psi @Temperature 1020 °F |
Annealed prior to test | |
| Elongation at Break | 45 % | 45 % | Annealed prior to test. |
| 45 % @Temperature 550 °C |
45 % @Temperature 1020 °F |
Annealed prior to test. |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 14.0 µm/m-°C @Temperature 20.0 - 100 °C |
7.78 µin/in-°F @Temperature 68.0 - 212 °F |
|
| Specific Heat Capacity | 0.440 J/g-°C | 0.105 BTU/lb-°F | |
| Thermal Conductivity | 11.1 W/m-K | 77.0 BTU-in/hr-ft²-°F | |
| Melting Point | 1370 - 1400 °C | 2500 - 2550 °F | |
| Solidus | 1370 °C | 2500 °F | |
| Liquidus | 1400 °C | 2550 °F |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Aluminum, Al | <= 0.20 % | <= 0.20 % | |
| Carbon, C | <= 0.050 % | <= 0.050 % | |
| Chromium, Cr | 19.5 - 23.5 % | 19.5 - 23.5 % | |
| Copper, Cu | 1.5 - 3.0 % | 1.5 - 3.0 % | |
| Iron, Fe | >= 22 % | >= 22 % | |
| Manganese, Mn | <= 1.0 % | <= 1.0 % | |
| Molybdenum, Mo | 2.5 - 3.5 % | 2.5 - 3.5 % | |
| Nickel, Ni | 38 - 46 % | 38 - 46 % | |
| Silicon, Si | <= 0.50 % | <= 0.50 % | |
| Sulfur, S | <= 0.030 % | <= 0.030 % | |
| Titanium, Ti | 0.60 - 1.2 % | 0.60 - 1.2 % |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 0.000113 ohm-cm | 0.000113 ohm-cm | |
| Magnetic Permeability | 1.005 | 1.005 | at 200 oersted (15.9 kA/m) |
| Curie Temperature | <= -196 °C | <= -321 °F |
Users viewing this material also viewed the following:
- Precision Polymer Engineering C40M Chloroprene Rubber
- Eastman Heatwave CF746 Polymer (discontinued **)
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 10 PHR Hi-Sil 233 Filler
- Lucas-Milhaupt SIL-FOS 6 Silver/ Copper/ Phosphorus Alloy
- Solvay TECHNYL® C 536XT PA6, DRY
- Tra-Con Tra-Bond FDA22 Food and Drug Application Epoxy Adhesive
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 75 PHR N990 Filler
- Colorite Polymers 6088 Non-Phthalate 88 Series Vinyl Compound
- BASF Capron® 8231G 14% Glass-Filled Nylon 6 (Conditioned) (discontinued **)
- Covestro Makrolon® LQ-2847 Polycarbonate, Lens Quality Optical, Mold Release, UV Stabilized (discontinued **)
Copyright © lookpolymers.com All Rights Reserved