Unitika A1025NO PA6, Flame Retardant, Dry
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced, Flame Retardant |
| Manufacturer | Unitika |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Unitika A1025NO PA6, Flame Retardant, Dry.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Unitika Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.34 g/cc | 0.0484 lb/in³ | ISO 1183 |
| Water Absorption | 1.2 % @Time 86400 sec |
1.2 % @Time 24.0 hour |
ISO 62 |
| Moisture Absorption at Equilibrium | 1.9 % | 1.9 % | 50% RH; ISO 62 |
| Linear Mold Shrinkage, Flow | 0.011 cm/cm @Thickness 3.20 mm |
0.011 in/in @Thickness 0.126 in |
|
| Linear Mold Shrinkage, Transverse | 0.015 cm/cm @Thickness 3.20 mm |
0.015 in/in @Thickness 0.126 in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 116 | 116 | ISO 2039 |
| Tensile Strength at Break | 77.0 MPa | 11200 psi | ISO 527-1/-2 |
| Elongation at Break | 3.4 % | 3.4 % | ISO 527-1/-2 |
| Tensile Modulus | 3.10 GPa | 450 ksi | ISO 527-1/-2 |
| Flexural Strength | 110 MPa | 16000 psi | ISO 178 |
| Flexural Modulus | 3.00 GPa | 435 ksi | ISO 178 |
| Charpy Impact Unnotched | 3.50 J/cm² | 16.7 ft-lb/in² | ISO 179-1 |
| Charpy Impact, Notched | 0.300 J/cm² | 1.43 ft-lb/in² | ISO 179-1 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 100 µm/m-°C | 55.6 µin/in-°F | ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 170 °C | 338 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 66.0 °C | 151 °F | ISO 75-1/-2 |
| Flammability, UL94 | V-0 @Thickness 0.840 mm |
V-0 @Thickness 0.0331 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | IEC 60093 |
| Dielectric Constant | 3.0 @Frequency 1.00e+6 Hz |
3.0 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Dielectric Strength | 25.0 kV/mm @Thickness 1.00 mm |
635 kV/in @Thickness 0.0394 in |
IEC 60243-1 |
| Dissipation Factor | 0.010 @Frequency 1.00e+6 Hz |
0.010 @Frequency 1.00e+6 Hz |
IEC 60250 |
Users viewing this material also viewed the following:
- Pinnacle Polymers 1512 Polypropylene Homopolymer, Fiber Spinning Grade
- LATI Latilub 66-10T K/10 PA66, 10% Carbon Fiber Reinforced, PTFE Filled
- A. Schulman POLYBATCH™ Green 3315 Concentrate Based In Polyethylene
- Trelleborg Emerson & Cuming Stycast® E 1400 Two-Component General Purpose Encapsulant
- A. Schulman POLYBATCH™ Dark Blue Oil LL40350/4 Concentrate Based In LLDPE
- Covestro Desmopan® 786 S Polyurethane
- Fainplast Compounds CL 70/2 Flexible PVC, Sheathing
- 3M FA102 Destructible Acetate Label Products
- Goodfellow Audiolloy® Iron 52/Nickel 48 Alloy
Copyright © lookpolymers.com All Rights Reserved