- Polycarbonate, 30% Glass Filled
- Samyang Trirex® 3500G30 Polycarbonate, 30% Glass Reinforced
Samyang Trirex® 3500G30 Polycarbonate, 30% Glass Reinforced
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, 30% Glass Filled |
| Manufacturer | Samyang |
| Trade Name | Trirex® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samyang Trirex® 3500G30 Polycarbonate, 30% Glass Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
TRIREX® polycarbonate resins offer superior transparency, mechanical properties, good dimensional stability and high electrical performance, which allows it to be widely used for electrical, electronic, appliance, automotive and optical industries.Characteristics:Medium viscosity30% glass fiberApplications:3025R type reinforced by glass fiber (short fiber). particularly suitable for injection molding where especially good dimensional stability is requiredAll information provided by Samyang
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.43 g/cc | 1.43 g/cc | ASTM D792 |
| Water Absorption | 0.15 % @Time 86400 sec |
0.15 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage | 0.0030 - 0.0050 cm/cm @Thickness 3.00 mm |
0.0030 - 0.0050 in/in @Thickness 0.118 in |
ASTM D955 |
| Melt Flow | 4.5 g/10 min @Load 1.20 kg, Temperature 300 °C |
4.5 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 122 | 122 | ASTM D785 |
| Tensile Strength, Yield | 127 MPa | 18500 psi | ASTM D638 |
| Elongation at Break | 9.0 % | 9.0 % | ASTM D638 |
| Flexural Yield Strength | 186 MPa | 27000 psi | ASTM D790 |
| Flexural Modulus | 6.86 GPa | 996 ksi | ASTM D790 |
| Izod Impact, Unnotched | 2.06 J/cm @Thickness 3.17 mm |
3.86 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 19.0 µm/m-°C | 10.6 µin/in-°F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 152 °C | 306 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 148 °C | 298 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 1.59 mm |
V-0 @Thickness 0.0625 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 4.00e+16 ohm-cm | 4.00e+16 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.29 @Frequency 1.00e+6 Hz |
3.29 @Frequency 1.00e+6 Hz |
ASTM D150 |
| Dielectric Strength | 31.0 kV/mm | 787 kV/in | ASTM D149 |
| Dissipation Factor | 0.0097 @Frequency 1.00e+6 Hz |
0.0097 @Frequency 1.00e+6 Hz |
ASTM D150 |
| Arc Resistance | 120 sec | 120 sec | ASTM D495 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 280 - 300 °C | 536 - 572 °F | |
| Middle Barrel Temperature | 280 - 300 °C | 536 - 572 °F | |
| Front Barrel Temperature | 280 - 300 °C | 536 - 572 °F | |
| Nozzle Temperature | 290 - 310 °C | 554 - 590 °F | |
| Melt Temperature | 300 - 310 °C | 572 - 590 °F | |
| Drying Temperature | 120 °C | 248 °F | |
| Dry Time | 3 - 5 hour | 3 - 5 hour | |
| Moisture Content | <= 0.020 % | <= 0.020 % | |
| Screw Speed | 30 - 80 rpm | 30 - 80 rpm |
Users viewing this material also viewed the following:
- Indium Corp. NanoFoil® High Temperature Nickel and Aluminum Sacrificial Heat Source
- H.C. Starck Type I Pure Molybdenum MIMP Powder
- H.C. Starck Grade AX 20 Silicon Metal Powder Si
- Shandong Guangyin PA 612 Nylon Resin
- A. Schulman POLYBATCH™ White LL8425 AP Concentrate Based In LLDPE
- Westlake EF412 Low Density Polyethylene
- Total EVA 1020 VN 5 Ethylene Vinyl Acetate Copolymer - Blown Film
- Hexcel® HexWeb® HRH-327 - 3/16 - 5.0 Fiberglass Reinforced Polyimide Honeycomb
- DuPont Performance Polymers Zytel® 80G14A NC010A Nylon 66 (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved