MRC Polymers MAXNITE™ 500 GF15 PET, 15% Glass Fiber Filled (discontinued **)
| Category | Polymer , Thermoplastic , Polyester, TP , Polyethylene Terephthalate (PET) , Polyethylene Terephthalate (PET), 20% Glass Reinforced |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | MRC Polymers MAXNITE™ 500 GF15 PET, 15% Glass Fiber Filled
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by MRC Polymers Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.43 g/cc | 1.43 g/cc | ASTM D792 |
| Filler Content | 13 - 17 % | 13 - 17 % | ASTM D2584 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 82.7 MPa | 12000 psi | ASTM D638 |
| Elongation at Break | 2.0 % | 2.0 % | ASTM D638 |
| Flexural Strength | 131 MPa | 19000 psi | ASTM D790 |
| Flexural Modulus | 5.86 GPa | 850 ksi | ASTM D790 |
| Izod Impact, Notched | 0.641 J/cm @Temperature 22.8 °C |
1.20 ft-lb/in @Temperature 73.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 260 - 282 °C | 500 - 540 °F | |
| Middle Barrel Temperature | 260 - 288 °C | 500 - 550 °F | |
| Front Barrel Temperature | 266 - 288 °C | 510 - 550 °F | |
| Nozzle Temperature | 271 - 299 °C | 520 - 570 °F | reverse tapered recommended |
| Melt Temperature | 271 - 293 °C | 520 - 560 °F | |
| Mold Temperature | 82.2 - 104 °C | 180 - 220 °F | thick wall - thin wall |
| Drying Temperature | 116 - 135 °C | 240 - 275 °F | |
| Dry Time | 4 - 6 hour | 4 - 6 hour | |
| Moisture Content | <= 0.020 % | <= 0.020 % | |
| Dew Point | <= -17.8 °C | <= 0.000 °F | |
| Drying Air Flow Rate | 22.7 - 28.3 l/min | 0.800 - 1.00 ft³/min (CFM) | per lb/hour resin processed |
| Injection Pressure | 68.9 - 138 MPa | 10000 - 20000 psi | |
| Back Pressure | 0.345 - 1.21 MPa | 50.0 - 175 psi | keep minimum |
| Cushion | 0.635 cm | 0.250 in | |
| Screw Speed | 20 - 50 rpm | 20 - 50 rpm |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Dryer | Dehumidified hopper | |
| Fill Rate | Moderate-Fast | |
| Hold Pressure | 40-60% of injection pressure | |
| Packing Pressure | 50-75% of injection pressure |
Users viewing this material also viewed the following:
- Nye Lubricants 435 (SO) Synthetic Oil
- PolyOne LubriOne™ PC-20GF/15T Polycarbonate (PC)
- SABIC Innovative Plastics Lexan® 141 PC
- Materion BrushCAST® 3C High Conductivity Casting Alloy (As Cast)
- Lord Adhesives Thermosetâ„¢ MD-140 Conductive Adhesive
- SABIC Innovative Plastics LNP LUBRICOMP KL004U Acetal Copolymer
- Dow Corning AMS-C30 Cosmetic Wax
- Dow Corning SYL-OFF® 7680-030 POLYMER
- Fainplast Compounds GK 80/R Flexible PVC, Flame Retardant Sheathing Lead Free
- 3M Super 77™ Multipurpose Spray Adhesive
Copyright © lookpolymers.com All Rights Reserved