Network Polymers SBS 1000 Clear Styrene Butadiene Copolymer
| Category | Polymer , Thermoplastic , Acrylic (PMMA) , Polystyrene (PS) , Styrene-Butadiene , Styrene-Butadiene Copolymer, SBC |
| Manufacturer | Network Polymers |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Network Polymers SBS 1000 Clear Styrene Butadiene Copolymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Clear Styrene Butadiene CopolymerInformation provided by Network Polymers Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.01 g/cc | 1.01 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0060 cm/cm | 0.0020 - 0.0060 in/in | ASTM D955 |
| Melt Flow | 11 g/10 min @Load 5.00 kg, Temperature 200 °C |
11 g/10 min @Load 11.0 lb, Temperature 392 °F |
Procedure A Condition G; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 60 - 70 | 60 - 70 | ASTM D2240 |
| Tensile Strength at Break | 22.8 MPa | 3300 psi | chs 2 in/min; ASTM D638 |
| Flexural Strength | 37.2 MPa | 5400 psi | Test Method I, Procedure B (chs speed 0.05 in/min); ASTM D790 |
| Flexural Modulus | 1.72 GPa | 250 ksi | Test Method I, Procedure B (chs speed 0.05 in/min); ASTM D790 |
| Izod Impact, Notched | 0.267 J/cm | 0.500 ft-lb/in | 0.125 inch bar; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 76.9 °C | 170 °F | 0.125 in bar; ASTM D648 |
| Vicat Softening Point | 90.7 °C | 195 °F | 0.125 inch bar, 1 Kg; ASTM D1525 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Transmission, Visible | 90 % | 90 % | clear; thickness not quantified |
Users viewing this material also viewed the following:
- Plenco 4224 Phenolic, Granular, Transfer Molded (discontinued **)
- Hybrid Plastics POSS® EP 1000 Epoxy Adhesive
- UBE UBEPOL BR150L Non-Oil Extended Synthetic Rubber Vulcanizate (Cured 35 Minutes at 145°C)
- ExxonMobil Vistalon™ 404 Ethylene Propylene Copolymer Rubber
- Esstech X-863-0050 Surface Active Monomer, NTG-GMA, Sodium Salt, C16H20NO5Na
- AdvanSource Biomaterials HYDROTHANE™ Hydrophilic Thermoplastic Polyurethane
- American Computer Optics UV Protection Glass 2 mm
- A. Schulman POLYFORT™ PP 3052UX Impact Resistant Copolymer
- Indium Corp. Indalloy 195 Gold Solder Alloy
- Industeel VIRGO 15.5PH 15Cr-5Ni-3Cu Precipitation Hardening Martensitic Stainless Steel (593°C - 4 hours - air cooling)
Copyright © lookpolymers.com All Rights Reserved