Toyobo GLAMIDE® T-665C30 Nylon-66

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Carbon Fiber Filled
Manufacturer Toyobo
Trade Name GLAMIDE®
Port Ningbo port,China
Trade Terms EXW, FOB, CFR, CIF
Payment Terms L/C, T/T, PayPal
Download PDF Toyobo GLAMIDE® T-665C30 Nylon-66.pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
GLAMIDE® is very tough and exhibits high abrasion resistance. It has a high melting point and heat resistance, has well-balanced proportions of mechanical properties, performs self-distinguishing and a specific grade approved as UL94V-0 class is provided, and it exhibits excellent chemical resistance and oil resistance. Grade T-665C30 is a CF reinforced Nylon-66. It has good electro-conductivity and contains 30% CF.30
Physical Properties Metric English Comments
Specific Gravity 1.27 g/cc
1.27 g/cc
Absolute Drying; ASTM-D792
Filler Content 30 %
30 %
Water Absorption 0.60 %
0.60 %
Absolute Drying; ASTM-D570
Moisture Absorption at Equilibrium 1.7 %
1.7 %
Absolute Drying; ASTM-D570
Linear Mold Shrinkage 0.0020 - 0.0050 cm/cm
<br>@Thickness 1.00 mm
 0.0020 - 0.0050 in/in
<br>@Thickness 0.0394 in
 Absolute Drying
0.0060 - 0.0090 cm/cm
<br>@Thickness 3.00 mm
 0.0060 - 0.0090 in/in
<br>@Thickness 0.118 in
 Absolute Drying
Mechanical Properties Metric English Comments
Hardness, Rockwell R 120
120
Absolute Drying; ASTM-D785
Tensile Strength, Ultimate 105 MPa
<br>@Temperature 80.0 °C
 15200 psi
<br>@Temperature 176 °F
 Practical Use (Water Absorption 1.75%); ASTM-D638
132 MPa
<br>@Temperature 80.0 °C
 19100 psi
<br>@Temperature 176 °F
 Absolute Drying; ASTM-D638
150 MPa
<br>@Temperature 23.0 °C
 21800 psi
<br>@Temperature 73.4 °F
 Practical Use (Water Absorption 1.75%); ASTM-D638
216 MPa
<br>@Temperature 23.0 °C
 31300 psi
<br>@Temperature 73.4 °F
 Absolute Drying; ASTM-D638
235 MPa
<br>@Temperature -40.0 °C
 34100 psi
<br>@Temperature -40.0 °F
 Practical Use (Water Absorption 1.75%); ASTM-D638
260 MPa
<br>@Temperature -40.0 °C
 37700 psi
<br>@Temperature -40.0 °F
 Absolute Drying; ASTM-D638
Elongation at Break 2.4 %
2.4 %
Absolute Drying; ASTM-D638
3.0 %
3.0 %
Practical Use (Water Absorption 1.75%); ASTM-D638
Flexural Strength 140 MPa
<br>@Temperature 80.0 °C
 20300 psi
<br>@Temperature 176 °F
 Practical Use (Water Absorption 1.75%); ASTM-D790
210 MPa
<br>@Temperature 80.0 °C
 30500 psi
<br>@Temperature 176 °F
 Absolute Drying; ASTM-D790
215 MPa
<br>@Temperature 23.0 °C
 31200 psi
<br>@Temperature 73.4 °F
 Practical Use (Water Absorption 1.75%); ASTM-D790
300 MPa
<br>@Temperature 23.0 °C
 43500 psi
<br>@Temperature 73.4 °F
 Absolute Drying; ASTM-D790
320 MPa
<br>@Temperature -40.0 °C
 46400 psi
<br>@Temperature -40.0 °F
 Practical Use (Water Absorption 1.75%); ASTM-D790
337 MPa
<br>@Temperature -40.0 °C
 48900 psi
<br>@Temperature -40.0 °F
 Absolute Drying; ASTM-D790
Flexural Modulus 7.20 GPa
<br>@Temperature 80.0 °C
 1040 ksi
<br>@Temperature 176 °F
 Practical Use (Water Absorption 1.75%); ASTM-D790
10.0 GPa
<br>@Temperature 23.0 °C
 1450 ksi
<br>@Temperature 73.4 °F
 Practical Use (Water Absorption 1.75%); ASTM-D790
10.0 GPa
<br>@Temperature 80.0 °C
 1450 ksi
<br>@Temperature 176 °F
 Absolute Drying; ASTM-D790
15.6 GPa
<br>@Temperature 23.0 °C
 2260 ksi
<br>@Temperature 73.4 °F
 Absolute Drying; ASTM-D790
17.2 GPa
<br>@Temperature -40.0 °C
 2490 ksi
<br>@Temperature -40.0 °F
 Practical Use (Water Absorption 1.75%); ASTM-D790
19.0 GPa
<br>@Temperature -40.0 °C
 2760 ksi
<br>@Temperature -40.0 °F
 Absolute Drying; ASTM-D790
Izod Impact, Notched 0.720 J/cm
<br>@Temperature -40.0 °C
 1.35 ft-lb/in
<br>@Temperature -40.0 °F
 Absolute Drying; ASTM-D256
0.800 J/cm
<br>@Temperature -40.0 °C
 1.50 ft-lb/in
<br>@Temperature -40.0 °F
 Practical Use (Water Absorption 1.75%); ASTM-D256
1.20 J/cm
<br>@Temperature 23.0 °C
 2.25 ft-lb/in
<br>@Temperature 73.4 °F
 Absolute Drying; ASTM-D256
1.50 J/cm
<br>@Temperature 23.0 °C
 2.81 ft-lb/in
<br>@Temperature 73.4 °F
 Practical Use (Water Absorption 1.75%); ASTM-D256
Taber Abrasion, mg/1000 Cycles 6.0
6.0
CS-17, Absolute Drying; ASTM-D1044
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 255 °C
491 °F
Absolute Drying; ASTM-D648
Flammability, UL94 HB
HB
Electrical Properties Metric English Comments
Volume Resistivity 0.010 ohm-cm
0.010 ohm-cm
Absolute Drying; ASTM-D257
Processing Properties Metric English Comments
Melt Temperature 270 - 300 °C
518 - 572 °F
Mold Temperature 60.0 - 140 °C
140 - 284 °F
Injection Pressure 30.0 - 60.0 MPa
4350 - 8700 psi