- Acrylonitrile Butadiene Styrene (ABS), Plating Grade
- Samsung Cheil Industries Starex® MP-0670 ABS, Metal Plating Grade
Samsung Cheil Industries Starex® MP-0670 ABS, Metal Plating Grade
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Plating Grade |
| Manufacturer | Samsung, Cheil Industries |
| Trade Name | Starex® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samsung Cheil Industries Starex® MP-0670 ABS, Metal Plating Grade.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Samsung Cheil Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.04 g/cc | 1.04 g/cc | ASTM D792 |
| Water Absorption | 0.30 % @Temperature 23.0 °C |
0.30 % @Temperature 73.4 °F |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0060 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0060 in/in @Thickness 0.126 in |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0060 cm/cm @Thickness 3.20 mm |
0.0060 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 2.3 g/10 min @Load 5.00 kg, Temperature 200 °C |
2.3 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 106 | 106 | ASTM D785 |
| Tensile Strength at Break | 35.3 MPa | 5120 psi | 5 mm/min; ASTM D638 |
| Tensile Strength, Yield | 44.1 MPa | 6400 psi | 5 mm/min; ASTM D638 |
| Elongation at Break | 25 % | 25 % | 5 mm/min; ASTM D638 |
| Tensile Modulus | 2.14 GPa | 310 ksi | 5 mm/min; ASTM D638 |
| Flexural Strength | 64.7 MPa | 9380 psi | 2.8 mm/min; ASTM D790 |
| Flexural Modulus | 2.11 GPa | 306 ksi | 2.8 mm/min; ASTM D790 |
| Izod Impact, Notched | 0.785 J/cm @Thickness 6.35 mm, Temperature -30.0 °C |
1.47 ft-lb/in @Thickness 0.250 in, Temperature -22.0 °F |
ASTM D256 |
| 0.883 J/cm @Thickness 3.17 mm, Temperature -30.0 °C |
1.65 ft-lb/in @Thickness 0.125 in, Temperature -22.0 °F |
ASTM D256 | |
| 2.65 J/cm @Thickness 6.35 mm, Temperature 23.0 °C |
4.96 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F |
ASTM D256 | |
| 2.84 J/cm @Thickness 3.17 mm, Temperature 23.0 °C |
5.33 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 88.0 °C @Thickness 6.40 mm |
190 °F @Thickness 0.252 in |
ASTM D648 |
| Vicat Softening Point | 100 °C | 212 °F | B/50; ISO R306 |
Users viewing this material also viewed the following:
- RheTech Products FT7011-01 Thermoplastic Polyolefin, Non-UV Stabilized, Black
- SABIC Innovative Plastics Lexan® EX1036T PC (Europe-Africa-Middle East)
- Solvay Engineered Polymers SEQUEL® 1402 TPO (discontinued **)
- Mearthane Durethaneâ„¢ C 60D Polyurethane
- Johnson Matthey Plumbsol Soft Solder/Flux
- A. Schulman PP 2175 Polypropylene High Flow Copolymer Polypropylene
- Toyobo TS501 PPS, 50% Glass Fiber Reinforced
- DuPont Performance Polymers Delrin® 527UVE RD402 Acetal (POM) (Unverified Data**)
- 3M Scotch-Weld™ 6111 Tan Bulk only Adhesive
- Polyram RamTal PM1113 Polyacetal Copolymer for Injection Molding
Copyright © lookpolymers.com All Rights Reserved