- Industeel SIRIUS 314 25% Cr - 1.8% Si Heat Resistant Stainless Steel
Industeel SIRIUS 314 25% Cr - 1.8% Si Heat Resistant Stainless Steel
| Category | Metal , Ferrous Metal , Austenitic , Stainless Steel , T 300 Series Stainless Steel |
| Manufacturer | Groupe Arcelor |
| Trade Name | SIRIUS |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Industeel SIRIUS 314 25% Cr - 1.8% Si Heat Resistant Stainless Steel.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: CLI SIRIUS 314 grade is a fully austenitic stainless steel containing 25% Cr, 20% Ni and 1.8% Si. The alloy is designed for high temperature corrosion resistance applications even in severe conditions. Carbon additions are optimized in order to increase creep properties and mechanical properties. The alloy is well designed for applications up to 1150°C (2102°F) in oxidizing atmospheres, or up to 1050°C (2012°F) in reducing atmospheres. Sulphur, carbon or nitrogen pick up reduce the behavior of the steel. The alloy performs better than Sirius 310 or Sirius 253 grades in most of the applications.Information provided by manufacturer.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 7.90 g/cc | 0.285 lb/in³ |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 600 MPa | 87000 psi | Typical after Solution Annealing |
| Tensile Strength, Yield | 285 MPa @Strain 0.200 % |
41300 psi @Strain 0.200 % |
Typical after Solution Annealing |
| 305 MPa @Strain 1.00 % |
44200 psi @Strain 1.00 % |
Typical after Solution Annealing | |
| Elongation at Break | 45 % | 45 % | Typical |
| Creep Strength | 130 MPa @Temperature 600 °C, Time 3.60e+6 sec |
18900 psi @Temperature 1110 °F, Time 1000 hour |
|
| Modulus of Elasticity | 200 GPa | 29000 ksi | |
| Poissons Ratio | 0.333 | 0.333 | Calculated |
| Shear Modulus | 75.0 GPa @Temperature 20.0 °C |
10900 ksi @Temperature 68.0 °F |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 16.0 µm/m-°C @Temperature 20.0 - 100 °C |
8.89 µin/in-°F @Temperature 68.0 - 212 °F |
|
| 17.0 µm/m-°C @Temperature 20.0 - 200 °C |
9.44 µin/in-°F @Temperature 68.0 - 392 °F |
||
| 18.0 µm/m-°C @Temperature 20.0 - 400 °C |
10.0 µin/in-°F @Temperature 68.0 - 752 °F |
||
| 18.5 µm/m-°C @Temperature 20.0 - 600 °C |
10.3 µin/in-°F @Temperature 68.0 - 1110 °F |
||
| Specific Heat Capacity | 0.500 J/g-°C @Temperature 20.0 °C |
0.120 BTU/lb-°F @Temperature 68.0 °F |
|
| Thermal Conductivity | 14.0 W/m-K @Temperature 20.0 °C |
97.2 BTU-in/hr-ft²-°F @Temperature 68.0 °F |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Carbon, C | <= 0.15 % | <= 0.15 % | |
| Chromium, Cr | 25 % | 25 % | |
| Iron, Fe | 53.05 - 53.2 % | 53.05 - 53.2 % | As remainder |
| Nickel, Ni | 20 % | 20 % | |
| Silicon, Si | 1.8 % | 1.8 % |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 0.0000950 ohm-cm @Temperature 20.0 °C |
0.0000950 ohm-cm @Temperature 68.0 °F |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® BPL1000 PC (Asia Pacific)
- Overview of materials for Acrylonitrile Butadiene Styrene (ABS), PTFE Filled
- M. Holland Company RP700 Polypropylene Copolymer
- Global PP-3200-H Polypropylene Random Copolymer
- Taiwan PU Corporation TPUI-H85 High Hydrolysis Resistance, Injection Molding Polyether Base TPU
- SABIC Innovative Plastics LNP LUBRILOY DF2049 PC (Asia Pacific)
- Amco PRIMATOP PP CO 350-40 Polypropylene Copolymer
- ATI Allegheny Ludlum AL 17-7™ High Strength Stainless Steel, UNS S17700
- A. Schulman POLYPUR™ FPU 1380 Thermoplastic Polyurethane Compound
Copyright © lookpolymers.com All Rights Reserved