Aclo Accutech Polypropylene Homopolymer HP0339C20L Calcium Reinforced
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 20% Calcium Carbonate (CaCO3) Filler |
| Manufacturer | Aclo Compounders |
| Trade Name | Accutech |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Aclo Accutech Polypropylene Homopolymer HP0339C20L Calcium Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.03 g/cc | 0.0372 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.012 cm/cm | 0.012 in/in | MD; ASTM D955 |
| Melt Flow | 21 g/10 min | 21 g/10 min | ASTM D1238 |
| Ash | 20 % | 20 % | ASTM D2584 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 91 | 91 | ASTM D785 |
| Tensile Strength at Break | 17.0 MPa | 2470 psi | ASTM D638 |
| Tensile Strength, Yield | 31.0 MPa | 4500 psi | ASTM D638 |
| Elongation at Break | 50 % | 50 % | ASTM D638 |
| Elongation at Yield | 6.0 % | 6.0 % | ASTM D638 |
| Tensile Modulus | 1.700 GPa | 246.5 ksi | ASTM D638 |
| Flexural Strength | 37.0 MPa | 5370 psi | ASTM D790 |
| Flexural Modulus | 1.60 GPa | 232 ksi | ASTM D790 |
| Izod Impact, Notched | 0.352 J/cm | 0.660 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 110 °C | 230 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C | 140 °F |
Users viewing this material also viewed the following:
- Indium Corp. Indalloy 128 Pure Tin
- Haynes Multimet® alloy, GTAW, 3.2 mm sheet
- Techmer ES Luriblend® PA6/6 CF30 TL15 HS BK 30% Carbon Filled
- SCG Chemicals EL-Proâ„¢ P842J Polypropylene Injection Molding
- Teknor Apex Monprene® MP-2455N Thermoplastic Elastomer
- A. Schulman PAPERMATCH® H-5338 Specialty Masterbatch
- EPICHEM Epiter PBT GF 20 Polybutylene Terephthalate, 20% Glass
- Fainplast Compounds HL 91/1 Flexible PVC, Insulation for High Temperatures
- ConocoPhillips Hydroclear® 460 Multipurpose R&O Oil, AGMA Lubricant No. 7
- Adell RR-19 Polypropylene Copolymer; 43% Glass Reinforced, High Impact
Copyright © lookpolymers.com All Rights Reserved