Teknor Apex Chemlon® 275H Nylon 6, Copolymer, Impact Modified
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Impact Grade |
| Manufacturer | Teknor Apex Company |
| Trade Name | Chemlon® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Teknor Apex Chemlon® 275H Nylon 6, Copolymer, Impact Modified.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Notes: Very high impact and elongation, low flexural modulus material for tubing and wire jacketing applications requiring a soft, flexible product; FMVSS Flammability: Passes, FMVSS 302Processing Method: Extrusion; Injection Molding Forms: Pellets Automotive Specifications: Chrysler MS-DB41 Type PA CPN2785 Color: BK001 Black; Ford ESB-M4D423-A2; Ford ESF-M4D423-A; Ford ESB-M4D426-A; GM GMP.PA6.003; GM GMP.PA6.004; Packard M-2170Information Provided by Teknor Apex
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.07 g/cc | 1.07 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.015 - 0.020 cm/cm | 0.015 - 0.020 in/in | ASTM D955 |
| Melt Flow | 3.0 g/10 min | 3.0 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 44.8 MPa | 6500 psi | ASTM D638 |
| Elongation at Break | 250 % | 250 % | ASTM D638 |
| Flexural Strength | 27.6 MPa | 4000 psi | ASTM D790 |
| Flexural Modulus | 0.0689 GPa | 10.0 ksi | ASTM D790 |
| Izod Impact, Notched | 10.1 J/cm @Temperature 22.8 °C |
19.0 ft-lb/in @Temperature 73.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 214 °C | 417 °F | DSC |
| Deflection Temperature at 0.46 MPa (66 psi) | 143 °C | 290 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 48.9 °C | 120 °F | Unannealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 216 - 235 °C | 420 - 455 °F | |
| Middle Barrel Temperature | 229 - 252 °C | 445 - 485 °F | |
| Front Barrel Temperature | 241 - 254 °C | 465 - 490 °F | |
| Nozzle Temperature | 241 - 254 °C | 465 - 490 °F | |
| Melt Temperature | 241 - 254 °C | 465 - 490 °F | Processing Temperature |
| Drying Temperature | 79.4 °C | 175 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Suggested Moisture, max | 0.15 | |
| Suggested Regrind, max | 25 |
Users viewing this material also viewed the following:
- Plastcom SLOVAMID 6 FRB 4 LS Polyamide 6, Halogen Free Flame Retardant, Light Stabilization
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 75 PHR Iceberg Clay Filler
- SABIC Innovative Plastics LNP LUBRICOMP EL002 PEI
- Hexcel® HexPly® F515 Epoxy Resin, T2C120 Carbon Tape
- ChevronTexaco Gear Compounds EP, ISO 100
- Entec Hyrene® PSCRY 14 General Purpose Polystyrene
- Chosun Refractories CRAG-S50 Long Stopper
- Arlon P31000A005 0.005" Uncured Silicone Rubber with PTFE Coated Fiberglass Carrier
- BASF Ultramid® A3X4G7 35% Glass Filled PA66 FR (Dry)
- Lehmann & Voss LUVOCOM® 1105-8344/GY PEEK, unreinforced
Copyright © lookpolymers.com All Rights Reserved