Teijin Panlite® BS-8120R Friction and Abrasion Resistant, Carbon Fiber Reinforced Polycarbonate Resin
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Carbon Fiber Reinforced |
| Manufacturer | Teijin |
| Trade Name | Panlite® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Teijin Panlite® BS-8120R Friction and Abrasion Resistant, Carbon Fiber Reinforced Polycarbonate Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
CF 20% reinforced grade, meeting UL 94 V-2. it is compounded with fluorine powder to improve friction and abrasion resistance and also exhibits a mold release property, maintaining excellent characteristics of polycarbonate resinApplications:Mechanical, electric and electronic components that need abrasion and friction resistance.Information provided by Teijin Chemicals Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.36 g/cc | 0.0491 lb/in³ | ISO 1183 |
| Water Absorption | 0.14 % | 0.14 % | in water, 23°C, 24h; ISO 62 |
| Linear Mold Shrinkage | 0.00020 - 0.0020 cm/cm @Thickness 4.00 mm |
0.00020 - 0.0020 in/in @Thickness 0.157 in |
|
| Linear Mold Shrinkage, Transverse | 0.0040 - 0.0060 cm/cm @Thickness 4.00 mm |
0.0040 - 0.0060 in/in @Thickness 0.157 in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 120 MPa | 17400 psi | 50mm/min; ISO 527 |
| Elongation at Break | 1.5 % | 1.5 % | 50mm/min; ISO 527 |
| Tensile Modulus | 13.6 GPa | 1970 ksi | 1mm/min; ISO 527 |
| Flexural Strength | 170 MPa | 24700 psi | 2mm/min; ISO 178 |
| Flexural Modulus | 12.0 GPa | 1740 ksi | 2mm/min; ISO 178 |
| Charpy Impact Unnotched | 2.50 J/cm² | 11.9 ft-lb/in² | ISO 179 |
| Charpy Impact, Notched | 0.700 J/cm² | 3.33 ft-lb/in² | ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 20.0 µm/m-°C @Temperature 20.0 °C |
11.1 µin/in-°F @Temperature 68.0 °F |
ISO 11359 |
| CTE, linear, Transverse to Flow | 60.0 µm/m-°C @Temperature 20.0 °C |
33.3 µin/in-°F @Temperature 68.0 °F |
ISO 11359 |
| Deflection Temperature at 0.46 MPa (66 psi) | 150 °C | 302 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 147 °C | 297 °F | ISO 75 |
| Vicat Softening Point | 152 °C | 306 °F | 50°C/hr, 50N; ISO 306 |
| UL RTI, Electrical | 80.0 °C @Thickness 1.47 mm |
176 °F @Thickness 0.0579 in |
UL 746B |
| UL RTI, Mechanical with Impact | 80.0 °C @Thickness 1.47 mm |
176 °F @Thickness 0.0579 in |
UL 746B |
| UL RTI, Mechanical without Impact | 80.0 °C @Thickness 1.47 mm |
176 °F @Thickness 0.0579 in |
UL 746B |
| Flammability, UL94 | V-2 @Thickness 0.750 mm |
V-2 @Thickness 0.0295 in |
|
| V-1 @Thickness 1.50 mm |
V-1 @Thickness 0.0591 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 0.10 - 10 ohm-cm | 0.10 - 10 ohm-cm | IEC 60093 |
| Surface Resistance | 1.0 - 100 ohm | 1.0 - 100 ohm | IEC 60093 |
Users viewing this material also viewed the following:
- Mytex Polymers AS65KW-1ATM Polypropylene, Talc filled, Compounded
- Silberline SilBerCote® PC 8152Z
- Teknor Apex Monprene® MP-1353A Thermoplastic Elastomer
- A. Schulman POLYFORT™ FPP 1007X Extra High Flow, Talc Fortified Homopolymer Polypropylene
- Chase Plastics CP Pryme® N120GL (COND, 50% RH) Nylon 6, 20% Glass Fiber Reinforced, Internally Lubricated
- Westlake Tymax™ GA7501 Anhydride Modified Acrylate Copolymer (Developmental)
- Chevron Phillips Marlex® HP132 High Density Polyethylene, Pressure Pipe Grade
- Entec Hypro™ PP-HP20NS Homopolymer, 20 Melt Flow, Nucleated, Anti-stat
- Arlon 30580R025 0.025" (0.635 mm) Uncured Unsupported Silicone Rubber on Release Carrier
Copyright © lookpolymers.com All Rights Reserved