- Vicone High Performance Rubber VicoSil™ 139DLK-CL High Performance Silicone Rubber
Vicone High Performance Rubber VicoSil™ 139DLK-CL High Performance Silicone Rubber
| Category | Polymer , Thermoset , Rubber or Thermoset Elastomer (TSE) , Silicone , Silicone Rubber |
| Manufacturer | Vicone High Performance Rubber |
| Trade Name | VicoSil™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Vicone High Performance Rubber VicoSil™ 139DLK-CL High Performance Silicone Rubber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
FDA Approved
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.19 g/cc | 0.0430 lb/in³ | ASTM D297 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 33 | 33 | ASTM D2240 |
| Tensile Strength | 4.50 MPa | 653 psi | ASTM D412 |
| Elongation at Break | 570 % | 570 % | ASTM D412 |
| Compressive Modulus | 0.00160 GPa @Strain 5 % |
0.232 ksi @Strain 5 % |
ISO-7743 |
| 0.00170 GPa @Strain 10 % |
0.247 ksi @Strain 10 % |
ISO-7743 | |
| 0.00180 GPa @Strain 20 % |
0.261 ksi @Strain 20 % |
ISO-7743 | |
| 0.00190 GPa @Strain 25 % |
0.276 ksi @Strain 25 % |
ISO-7743 | |
| Compression Set | 20 % | 20 % | ASTM D395 |
| Tensile Set | 5.1 % | 5.1 % | ASTM D412 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Transmission, Visible | 80 % | 80 % | clear grade; thickness not known |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Clear | |
| Effect of Liquids - Change in Elongation (%) | -7.2 | ASTM D471 |
| Effect of Liquids - Change in Hardness (%) | -7.5 | ASTM D471 |
| Effect of Liquids - Change in Tensile Strength (%) | -6.8 | ASTM D471 |
| Effect of Liquids - Change in Volume after Oil Immersion (%) | 6.9 | ASTM D471 |
| Heat Aging - Change in Elongation (%) | -29 | ASTM D573 |
| Heat Aging - Change in Hardness (%) | 7 | ASTM D573; 200°C; 72h |
| Heat Aging - Change in Tensile Strength (%) | -17 | ASTM D573 |
Users viewing this material also viewed the following:
- PolyOne LubriOne™ AT-000/05T 2S Acetal (POM) Copolymer
- Osprey Metals Co452 Cobalt Alloy Powder (Grade 90% - 16)
- Ravago Manufacturing Americas Hylon® N2000STL Nylon 6 (Cond)
- Overview of materials for Polybutylene Terephthalate (PBT), 30% Glass Fiber Filled
- SABIC Innovative Plastics LNP LUBRICOMP AL002 ABS
- Gromax BFG50-AH00B2 Nylon 6 50% Glass Filled (Conditioned)
- Haynes 214® alloy, 30% cold reduction, 925°C for 5 minutes
- Specialty Materials 5505 Boron Epoxy Prepreg Tape
- Eurostar Starflam AFR200Y PA66, Flame Retardant, Injection Molding
- 3M 9671 Adhesive Transfer Tapes with Adhesive 300
Copyright © lookpolymers.com All Rights Reserved