SABIC Innovative Plastics LNP THERMOCOMP WX05502 Polyester Elastomer
| Category | Polymer , Thermoplastic , Polyester, TP |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP WX05502 Polyester Elastomer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP THERMOCOMP* WX05502 is a compound based on Polyester, TP resin containing Flame Retardant, Glass Fiber, Mineral. Added features of this material include: Flame Retardant.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.81 g/cc | 1.81 g/cc | ASTM D792 |
| Density | 1.80 g/cc | 0.0650 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.0200 % | 0.0200 % | 50% RH, 24 hrs; ASTM D570 |
| 0.0300 % | 0.0300 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0050 cm/cm @Time 86400 sec |
0.0030 - 0.0050 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.030 cm/cm @Time 86400 sec |
0.010 - 0.030 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 85.0 MPa | 12300 psi | 5 mm/min; ISO 527 |
| 90.0 MPa | 13100 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 1.2 % | 1.2 % | 5 mm/min; ISO 527 |
| 1.4 % | 1.4 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 1.2 % | 1.2 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 11.74 GPa | 1703 ksi | 1 mm/min; ISO 527 |
| 13.24 GPa | 1920 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 141 MPa | 20500 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 142 MPa | 20600 psi | ISO 178 | |
| Flexural Modulus | 10.9 GPa | 1580 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 11.38 GPa | 1651 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.180 J/cm | 0.337 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 3.37 J/cm | 6.31 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² | 1.90 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 22.0 kJ/m² | 10.5 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 8.00 J @Temperature 23.0 °C |
5.90 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 1.00 J | 0.738 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 21.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
11.7 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 50.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
27.8 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 217 °C | 423 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 221 °C @Thickness 3.20 mm |
430 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 197 °C | 387 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 205 °C @Thickness 3.20 mm |
401 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- PPT LSF120 Low Sintering Temperature Ferrite Powder
- Nanocyl PLASTICYL™ PA1501 Polyamide 66 with 2 wt% Multi-Wall Carbon Nanotubes
- Polimeri Europa EDISTIR N1461 Polystyrene (discontinued **)
- Lubriplate 1200-2 Lithium Type Multi-Purpose Grease
- Lucite International Elvacite ® 2550 Acrylic Resin
- Special Metals NIMONIC® Alloy 75
- Teknor Apex Flexalloy® 9609-80 Polyvinyl Chloride Compound
- SABIC Innovative Plastics NORYL GFN1740V PPE+PS (Asia Pacific)
- 3M 410M Double Coated Paper Tapes
- 3M 1449 General Purpose Aluminum Foil Tape
Copyright © lookpolymers.com All Rights Reserved