Samsung Cheil Industries Starex® TF-0956 HI-PMMA

Category Polymer , Thermoplastic , Acrylic (PMMA) , Acrylic, Impact Modified, Molded
Manufacturer Samsung, Cheil Industries
Trade Name Starex®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Samsung Cheil Industries Starex® TF-0956 HI-PMMA.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by Samsung Cheil Industries.
Physical Properties Metric English Comments
Specific Gravity 1.16 g/cc
1.16 g/cc
ASTM D792
Linear Mold Shrinkage, Flow 0.0040 - 0.0080 cm/cm

@Thickness 3.20 mm
 0.0040 - 0.0080 in/in

@Thickness 0.126 in
 ASTM D955
Melt Flow 3.0 g/10 min

@Load 3.80 kg,
Temperature 230 °C
 3.0 g/10 min

@Load 8.38 lb,
Temperature 446 °F
 ASTM D1238
7.0 g/10 min

@Load 10.0 kg,
Temperature 220 °C
 7.0 g/10 min

@Load 22.0 lb,
Temperature 428 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 115
115
ASTM D785
Tensile Strength, Yield 52.0 MPa
7540 psi
5 mm/min; ASTM D638
Flexural Strength 72.6 MPa
10500 psi
2.8 mm/min; ASTM D790
Flexural Modulus 1.96 GPa
284 ksi
2.8 mm/min; ASTM D790
Izod Impact, Notched 0.441 J/cm

@Thickness 6.35 mm
 0.827 ft-lb/in

@Thickness 0.250 in
 ASTM D256
0.490 J/cm

@Thickness 3.17 mm
 0.918 ft-lb/in

@Thickness 0.125 in
 ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 78.0 °C

@Thickness 6.40 mm
 172 °F

@Thickness 0.252 in
 ASTM D648
Vicat Softening Point 93.0 °C
199 °F
B/50; ISO R306
Flammability, UL94 HB

@Thickness 1.50 - 3.00 mm
 HB

@Thickness 0.0591 - 0.118 in