Techmer ES Luriblend® PA6/6 GF30 TS15 30% Glass Filled
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled , Nylon 66, Heat Stabilized , Nylon 66, PTFE Filled |
| Manufacturer | Techmer ES |
| Trade Name | Luriblend® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Techmer ES Luriblend® PA6/6 GF30 TS15 30% Glass Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber, 30% Filler by WeightAdditive: Heat Stabilizer, Silicone Lubricant and PTFE Lubricant(15%)Features: Lubricated, Good Wear Resistance, Low Friction and Heat StabilizedInformation provided by TP Composites, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.47 g/cc | 0.0531 lb/in³ | ASTM D792 |
| Water Absorption | 0.50 % @Time 86400 sec |
0.50 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0040 cm/cm @Thickness 3.17 mm |
0.0040 in/in @Thickness 0.125 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 110 | 110 | ASTM D785 |
| Tensile Strength, Yield | 156 MPa | 22600 psi | ASTM D638 |
| Elongation at Break | 2.0 % | 2.0 % | ASTM D638 |
| Flexural Strength | 214 MPa | 31000 psi | ASTM D790 |
| Flexural Modulus | 8.96 GPa | 1300 ksi | ASTM D790 |
| Izod Impact, Notched | 0.908 J/cm @Thickness 3.17 mm |
1.70 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Coefficient of Friction, Dynamic | 0.25 | 0.25 | ASTM D1894 |
| Coefficient of Friction, Static | 0.20 | 0.20 | ASTM D1894 |
| K (wear) Factor | 36.3 x 10-8 mm³/N-M | 18.0 x 10-10 in³-min/ft-lb-hr | |
| Limiting Pressure Velocity | 0.596 MPa-m/sec | 17000 psi-ft/min | 10 fpm |
| 0.596 MPa-m/sec | 17000 psi-ft/min | 1000 fpm | |
| 0.666 MPa-m/sec | 19000 psi-ft/min | 100 fpm |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 23.4 µm/m-°C | 13.0 µin/in-°F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 252 °C | 485 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 241 °C | 465 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | ASTM D257 |
| Dielectric Strength | 19.7 kV/mm | 500 kV/in | Method A (Short-Time); ASTM D149 |
Users viewing this material also viewed the following:
- Radici Heraflex® A 55 I RKT TPS-SEBS Thermoplastic Elastomer
- Polymer Resources PPX-FR2 Modified-PPO, V-1 Flame Retardant
- Karina 810-37/3-CRB Ocher PVC Compound
- SABIC Innovative Plastics NORYL GTX GTX974 PPE+PA (Europe-Africa-Middle East)
- SABIC Innovative Plastics XYLEX X8210 PC+POLYESTER
- ChevronTexaco TDH® W Oil
- Aclo Accutech Polypropylene Homopolymer HP0336G5M25CL Glass/Mineral Reinforced Coupled
- Braskem TI2350C High Crystallinity Copolymer Polypropylene
- A. Schulman POLYBATCH™ U-0294-L Blowing Agent Concentrate Based In PE
- BASF 2-Ethyl Imidazole
Copyright © lookpolymers.com All Rights Reserved