Solvay TECHNYL® eXten D218 V30 Nylon 6.10, 30% glass fiber, DRY
| Category | Polymer , Thermoplastic , Nylon , Nylon 610 , Nylon 610, Glass Reinforced |
| Manufacturer | Solvay |
| Trade Name | Technyl® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay TECHNYL® eXten D218 V30 Nylon 6.10, 30% glass fiber, DRY.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: TECHNYL® eXten D 218 V30 is a 30% Glass Fiber reinforced and heat stabilized product suitable to the manufacturing of all injection molded parts. This material is available in black.Available in: Asia Pacific, Europe, Latin America and North AmericaProduct Applications: TECHNYL® eXten D 218 V30 is suitable to the manufacturing of injection molded parts in all sectors of applications. It offers excellent chemical resistance, low water absorption, very good mechanical properties and mold ability.Information provided by Rhodia, Rhodia has been acquired by Solvay.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.30 g/cc | 0.0470 lb/in³ | ISO 1183/A |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 152 MPa | 22000 psi | ISO 527 Type 1A |
| Elongation at Break | 4.4 % | 4.4 % | ISO 527 Type 1A |
| Tensile Modulus | 8.50 GPa | 1230 ksi | ISO 527 Type 1A |
| Flexural Strength | 250 MPa | 36300 psi | ISO 178 |
| Flexural Modulus | 8.00 GPa | 1160 ksi | ISO 178 |
| Charpy Impact Unnotched | 8.50 J/cm² @Temperature -30.0 °C |
40.4 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU |
| 9.00 J/cm² @Temperature 23.0 °C |
42.8 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 1.00 J/cm² @Temperature -30.0 °C |
4.76 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| 1.40 J/cm² @Temperature 23.0 °C |
6.66 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 215 °C | 419 °F | ISO 11357 |
| Deflection Temperature at 1.8 MPa (264 psi) | 195 °C | 383 °F | ISO 75/Af |
| Flammability, UL94 | HB @Thickness 0.800 mm |
HB @Thickness 0.0315 in |
ISO 1210 |
| HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
ISO 1210 | |
| HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
ISO 1210 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 225 - 230 °C | 437 - 446 °F | |
| Mold Temperature | 80.0 - 100 °C | 176 - 212 °F | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Moisture Content | <= 0.20 % | <= 0.20 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Compression Zone | 230-240°C | |
| Mixing Zone | 240-250°C |
Users viewing this material also viewed the following:
- Plastcom SLOVALEN PH 59 GF 30 PP, 30% glass fibre
- Solvay Specialty Polymers Ixef® 1524 Polyarylamide (PARA), 50% Glass Fiber (Conditioned)
- Solvay Specialty Polymers KetaSpire® KT-880 GF20 Polyetheretherketone (PEEK), 20% Glass Fiber
- SABIC Innovative Plastics LNP THERMOCOMP KX97390 Acetal Copolymer
- Wico Plast Wicoran 47 ABS, Impact Resistant
- Hexcel® HexForce™ 1659 Fiber Glass Fabric
- Total HDPE 7195 High Density Polyethylene, Specialty Extrusion Resin
- Asahi Glass Fluon® PB2015 15% Graphite, PTFE Filled Compound
Copyright © lookpolymers.com All Rights Reserved