Techmer ES Luriblend® PA6 GL15 Nylon 6
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced |
| Manufacturer | Techmer ES |
| Trade Name | Luriblend® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Techmer ES Luriblend® PA6 GL15 Nylon 6.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Availability: North AmericaForms: PelletsAdditive: Graphite Powder Lubricant(15%)Features: LubricatedInformation provided by TP Composites, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.22 g/cc | 0.0441 lb/in³ | ASTM D792 |
| Water Absorption | 1.0 % @Time 86400 sec |
1.0 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0090 cm/cm @Thickness 3.17 mm |
0.0090 in/in @Thickness 0.125 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 118 | 118 | ASTM D785 |
| Tensile Strength, Yield | 65.5 MPa | 9500 psi | ASTM D638 |
| Elongation at Break | 8.0 % | 8.0 % | ASTM D638 |
| Flexural Strength | 93.1 MPa | 13500 psi | ASTM D790 |
| Flexural Modulus | 3.65 GPa | 530 ksi | ASTM D790 |
| Izod Impact, Notched | 0.374 J/cm @Thickness 3.17 mm |
0.700 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 59.4 µm/m-°C | 33.0 µin/in-°F | ASTM D696 |
| Melting Point | 220 °C | 428 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 188 °C | 370 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 82.2 °C | 180 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | HB | HB |
Users viewing this material also viewed the following:
- Firestone C212-15C Nylon 6, Heat Stabilized
- Michelman® Michem® Emulsion 43240 Polypropylene emulsion
- SABIC Innovative Plastics LNP LUBRICOMP KL003 Acetal Copolymer (Asia Pacific)
- A. Schulman SCHULADUR® A GF50 50% Glass Fiber Reinforced PBT
- EMS-Grivory Grivory® GVX-65 H black 9915 PA*-GF65
- Cheng Yu Plastic IPS610BK Electric Conducting HIPS, Extrusion
- Zircar Ceramics AL-CEM Alumina Cement
- DuPont Performance Polymers VTR 8525 (GBLT-S) Peroxide Cured Fluoroelastomer (FKM) Formulation (discontinued
Copyright © lookpolymers.com All Rights Reserved