Latrobe MP35N® Alloy

Category Metal , Nonferrous Metal , Cobalt Alloy , Nickel Alloy
Manufacturer Latrobe Steel
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Latrobe MP35N® Alloy.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
MP35N is a nickel-cobalt base alloy of the Multiphase alloy system that has a unique combination of properties - ultra high strength, toughness, ductility, and outstanding corrosion resistance. The alloy is work-strengthened and aged to obtain strength levels of 260 to 300 ksi. MP35N alloy resists corrosion in hydrogen sulfide, salt water and other chloride solutions, as well as the mineral acids. It has exceptional resistance to crevice and stress corrosion cracking in sea water and other hostile environments.Information Provided by Timken Latrobe Steel.Timken sold Latrobe in December 2006. They are now Latrobe Specialty Steels Co.
Physical Properties Metric English Comments
Density 8.55 g/cc
0.309 lb/in³
Mechanical Properties Metric English Comments
Hardness, Rockwell B 90
90
Annealed
Tensile Strength, Ultimate 896 MPa
130000 psi
Annealed
Tensile Strength, Yield 379 MPa

@Strain 0.200 %
 55000 psi

@Strain 0.200 %
 Annealed
Elongation at Break 65 %
65 %
Annealed; in 4D
Reduction of Area 75 %
75 %
Modulus of Elasticity 232.8 GPa
33760 ksi
Annealed
234.8 GPa
34050 ksi
Cold Worked and Aged
201.0 GPa

@Temperature 482 °C
 29150 ksi

@Temperature 900 °F
 Annealed
201.3 GPa

@Temperature 482 °C
 29190 ksi

@Temperature 900 °F
 Cold Worked and Aged
Shear Modulus 67.8 GPa

@Temperature 482 °C
 9830 ksi

@Temperature 900 °F
 Cold Worked and Aged
70.60 GPa

@Temperature 482 °C
 10240 ksi

@Temperature 900 °F
 Annealed
80.94 GPa

@Temperature 25.6 °C
 11740 ksi

@Temperature 78.0 °F
 Cold Worked and Aged
83.36 GPa

@Temperature 25.6 °C
 12090 ksi

@Temperature 78.0 °F
 Annealed
Thermal Properties Metric English Comments
CTE, linear 11.2 µm/m-°C

@Temperature -100 - 121 °C
 6.22 µin/in-°F

@Temperature -148 - 250 °F
13.7 µm/m-°C

@Temperature 21.0 - 204 °C
 7.61 µin/in-°F

@Temperature 69.8 - 399 °F
15.7 µm/m-°C

@Temperature 21.0 - 538 °C
 8.72 µin/in-°F

@Temperature 69.8 - 1000 °F
Thermal Conductivity 6.50 W/m-K

@Temperature -184 °C
 45.1 BTU-in/hr-ft²-°F

@Temperature -299 °F
15.0 W/m-K

@Temperature 204 °C
 104 BTU-in/hr-ft²-°F

@Temperature 399 °F
Melting Point 1315 - 1440 °C
2399 - 2620 °F
Solidus 1315 °C
2399 °F
Liquidus 1440 °C
2620 °F
Component Elements Properties Metric English Comments
Chromium, Cr 20 %
20 %
Cobalt, Co 35 %
35 %
Molybdenum, Mo 10 %
10 %
Nickel, Ni 35 %
35 %
Electrical Properties Metric English Comments
Electrical Resistivity 0.0000986 ohm-cm

@Temperature -184 °C
 0.0000986 ohm-cm

@Temperature -299 °F
0.0001011 ohm-cm

@Temperature -73.0 °C
 0.0001011 ohm-cm

@Temperature -99.4 °F
0.0001033 ohm-cm

@Temperature 20.0 °C
 0.0001033 ohm-cm

@Temperature 68.0 °F
0.0001051 ohm-cm

@Temperature 93.0 °C
 0.0001051 ohm-cm

@Temperature 199 °F
0.0001078 ohm-cm

@Temperature 204 °C
 0.0001078 ohm-cm

@Temperature 399 °F
0.0001104 ohm-cm

@Temperature 316 °C
 0.0001104 ohm-cm

@Temperature 601 °F
0.0001179 ohm-cm

@Temperature 649 °C
 0.0001179 ohm-cm

@Temperature 1200 °F
Magnetic Permeability 1.00085
1.00085
At 392K
1.00142
1.00142
At 78K
Magnetic Susceptibility 8.03
8.03
At 392K
13.47
13.47
At 78K