Plenco 6553 Phenolic, Granular, Compression Molded

Category Polymer , Thermoset , Phenolic , Phenolic; Unreinforced; Molded
Manufacturer Plenco (Plastics Engineering Company)
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Plenco 6553 Phenolic, Granular, Compression Molded.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Two-Stage Phenolic. PLENCO 06553 is a phenolic molding compound, formulated specifically for automotive brake pistons. 06553 exhibits excellent dimensional stability, and resistance to brake fluids, and provides for grinding to close tolerances.Information supplied by Plenco
Physical Properties Metric English Comments
Density 2.13 g/cc
0.0770 lb/in³
ASTM D792
Apparent Bulk Density 1.01 g/cc
0.0365 lb/in³
Apparent density per ASTM D1895
Water Absorption 0.030 %
0.030 %
ASTM D570
Linear Mold Shrinkage 0.00040 cm/cm
0.00040 in/in
per ATM D955. Post shrinkage is 0.04% at 72hr 120ºC per ASTM D1299.
Mechanical Properties Metric English Comments
Hardness, Rockwell E 88
88
ASTM D785
Tensile Strength, Ultimate 53.5 MPa
7760 psi
ASTM D638
Tensile Modulus 4.10 GPa
595 ksi
ASTM D638
Flexural Yield Strength 89.9 MPa
13000 psi
ASTM D790
Flexural Modulus 19.03 GPa
2760 ksi
ASTM D790
Compressive Yield Strength 183.3 MPa
26590 psi
ASTM D695
Izod Impact, Notched 0.220 J/cm
0.412 ft-lb/in
ASTM D256
Charpy Impact, Notched 0.270 J/cm²
1.28 ft-lb/in²
ASTM D256
Impact 44
44
J/m Plenco drop ball test
Thermal Properties Metric English Comments
Thermal Conductivity 0.940 W/m-K

@Temperature 100 °C
6.52 BTU-in/hr-ft²-°F

@Temperature 212 °F
Maximum Service Temperature, Air 219 °C
426 °F
Heat resistance per ASTM D794
Deflection Temperature at 1.8 MPa (264 psi) 226 °C
439 °F
ASTM D648
Flammability, UL94 V-0

@Thickness 1.47 mm
V-0

@Thickness 0.0579 in
Oxygen Index 46 %
46 %
ASTM D2863
Electrical Properties Metric English Comments
Electrical Resistivity 6.89e+12 ohm-cm
6.89e+12 ohm-cm
ASTM D257
Dielectric Constant 5.4

@Frequency 1e+6 Hz
5.4

@Frequency 1e+6 Hz
ASTM D150
Dielectric Strength 11.2 kV/mm
284 kV/in
Short Time; ASTM D149
Dissipation Factor 0.019

@Frequency 1e+6 Hz
0.019

@Frequency 1e+6 Hz
ASTM D150
Arc Resistance 190 sec
190 sec
ASTM D495
Comparative Tracking Index 200 V
200 V
ASTM D3638