Toyobo PELPRENE™ P90BD Polyester TPE, High Viscous, High Durability
| Category | Polymer , Thermoplastic , Elastomer, TPE , Polyester TPE , Polyester, TP , Polyester Thermoplastic Elastomer |
| Manufacturer | Toyobo |
| Trade Name | Pelprene™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Toyobo PELPRENE™ P90BD Polyester TPE, High Viscous, High Durability.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Features: Polyester TPE, High Viscous, High DurabilityInformation provided by Toyobo.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.19 g/cc | 0.0430 lb/in³ | ASTM D792 |
| Moisture Absorption at Equilibrium | 0.40 % | 0.40 % | 23°C, 65% RH |
| Linear Mold Shrinkage | 0.011 cm/cm @Thickness 2.00 mm |
0.011 in/in @Thickness 0.0787 in |
|
| Melt Index of Compound | 3.0 g/10 min @Temperature 230 °C |
3.0 g/10 min @Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 96 | 96 | JIS K6301 |
| Hardness, Shore D | 57 | 57 | ASTM D2240 |
| Tensile Strength at Break | 31.4 MPa | 4550 psi | ASTM D638 |
| Elongation at Break | 700 % | 700 % | ASTM D638 |
| 50% Modulus | 0.0152 GPa | 2.20 ksi | ASTM D638 |
| Flexural Modulus | 0.162 GPa | 23.5 ksi | ASTM D790 |
| Compressive Modulus | 0.0133 GPa | 1.93 ksi | 0.1; ASTM D695 |
| Resilience | 65 | 65 | JIS K6301 |
| Izod Impact, Notched | NB | NB | ASTM D256 |
| Tear Strength | 172 kN/m | 981 pli | ASTM D624 |
| Taber Abrasion, mg/1000 Cycles | 13 | 13 | ASTM D1044 |
| Compression Set | 57 % | 57 % | JIS K6301 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 140 µm/m-°C @Temperature 20.0 °C |
77.8 µin/in-°F @Temperature 68.0 °F |
TMA |
| Melting Point | 203 °C | 397 °F | By DSC |
| Maximum Service Temperature, Air | 101 °C | 214 °F | Heat deflection temperature, load unknown; ASTM D648 |
| Vicat Softening Point | 180 °C | 356 °F | ASTM D1525 |
| Brittleness Temperature | <= -65.0 °C | <= -85.0 °F | JIS K6301 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 6.00e+13 ohm-cm | 6.00e+13 ohm-cm | ASTM D257 |
| Dielectric Strength | 30.0 kV/mm | 762 kV/in | JIS K2111 |
Users viewing this material also viewed the following:
- Polimeri Europa Flexirene® FG 23 I Butene Copolymer Linear Low Density Polyethylene
- LG Chemical LUTENE XL2808BK PE Compound
- Saint-Gobain Norton® T-200 Mechanical Grade PTFE Sheet (0.062" thick)
- SABIC Innovative Plastics Valox® IQNH4550 PBT (Europe-Africa-Middle East)
- Zircar Ceramics HR-3A Dense Aluminum Oxide Support Rod
- A. Schulman FORMION™ FI 397 Ionomer
- Eastman Tenite Propionate 360E0096907 Natural, Trsp Cellulose Acetate Propionate
- Chem Polymer Chemlon 256 Nylon 6, Wire Jacketing Grade
- Von Roll Isola IMI Varnish 73527 Solventless Polyester Varnish for Electrical Insulation
Copyright © lookpolymers.com All Rights Reserved