Techmer ES HiFill® HDPE TM30 30% Talc Filled
| Category | Polymer , Thermoplastic , Polyethylene (PE) , HDPE |
| Manufacturer | Techmer ES |
| Trade Name | HiFill® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Techmer ES HiFill® HDPE TM30 30% Talc Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Availability: North AmericaForms: PelletsFiller/Reinforcement: Talc Filler, 30% Filler by WeightInformation provided by TP Composites, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in³ | ASTM D792 |
| Water Absorption | 0.025 % @Time 86400 sec |
0.025 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.015 cm/cm @Thickness 3.17 mm |
0.015 in/in @Thickness 0.125 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 70 | 70 | ASTM D785 |
| Tensile Strength, Yield | 30.3 MPa | 4400 psi | ASTM D638 |
| Elongation at Break | 12 % | 12 % | ASTM D638 |
| Flexural Strength | 448 MPa | 65000 psi | ASTM D790 |
| Flexural Modulus | 1.38 GPa | 200 ksi | ASTM D790 |
| Izod Impact, Notched | 0.374 J/cm @Thickness 3.17 mm |
0.700 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Izod Impact, Unnotched | 4.27 J/cm @Thickness 3.17 mm |
8.00 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 81.0 µm/m-°C | 45.0 µin/in-°F | ASTM D696 |
| Melting Point | 135 °C | 275 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 98.9 °C | 210 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 65.6 °C | 150 °F | Unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Dielectric Strength | 19.7 kV/mm | 500 kV/in | Method A (Short-Time); ASTM D149 |
Users viewing this material also viewed the following:
- Potters Industries Q-Cel® 300
- SABIC Innovative Plastics LNP LUBRICOMP DL0029E PC
- Ineos K38-20-188 HDPE
- LATI Latamid 6 CUVHPX10 G/35 PA 6, 30% Glass Fiber Reinforced, Heat Stabilized
- Solvay TECHNYL® C 246 M PA6, Conditioned
- DuPont Performance Polymers Delrin® 127UV NC010 Acetal (POM) (Unverified Data**)
- Addcomp PRIEX® 25097 Maleic Anhydride Grafted PP random copolymer
- Westlake EMAC® SP2261 23% Ethylene-Methyl Acrylate Copolymer
- LATI Latimass 52/35-04 D009 PP Homopolymer
Copyright © lookpolymers.com All Rights Reserved