Radici Heraflex® E 7722 TPC-ET Thermoplastic Elastomer
| Category | Polymer , Thermoplastic , Elastomer, TPE |
| Manufacturer | Radici Group Plastics |
| Trade Name | Heraflex® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Radici Heraflex® E 7722 TPC-ET Thermoplastic Elastomer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
TPC-ET Thermoplastic Elastomer. High Modulus, Nominal Shore D/15s 69. Natural colorProcessing technology: Injection moldingInformation provided by Radici group.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.25 g/cc | 1.25 g/cc | |
| Water Absorption | 0.10 % @Time 86400 sec |
0.10 % @Time 24.0 hour |
MI / 08 |
| Melt Flow | 19 g/10 min @Load 2.16 kg, Temperature 230 °C |
19 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 77 | 77 | Instantaneous; ISO 868 |
| 69 @Time 15.0 sec |
69 @Time 0.00417 hour |
ISO 868 | |
| Tensile Strength at Break | 50.0 MPa | 7250 psi | ISO 527-1/2 |
| Elongation at Break | 500 % | 500 % | ISO 527 1/2 |
| Flexural Modulus | 0.828 GPa | 120 ksi | ISO 178/1A |
| Izod Impact, Notched | 3.00 J/cm | 5.62 ft-lb/in | ASTM D256 |
| Tear Strength | 249 kN/m | 1420 pli | ASTM D1004 |
| Abrasion | 39 | 39 | mm<sup>3</sup>; DIN 53516 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 220 °C | 428 °F | |
| Vicat Softening Point | 211 °C @Load 5.10 kg |
412 °F @Load 11.2 lb |
50°C/h |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Comparative Tracking Index | 600 V | 600 V |
Users viewing this material also viewed the following:
- Solvay Specialty Polymers AvaSpire® AV-742 SL30 Polyaryletherketone (PAEK) (Unverified Data**)
- Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 871°C (1600°F), aged 16000 hours
- Isoflon Tisoflon® 14G Polytetrafluoroethylene & Graphite Coated Glass Fabric
- Heatbath/Park Alu-Braze 960 Aluminum Brazing Salt
- ChevronTexaco Geotex® HD SAE 40
- Dymax 9-20496-Rev A HGA and OHGA Disk Drive Adhesive
- Blue River Coatings Acrylic 4000D Topcoat
- 3M Dynamar™ RC 5110 Rubber Curative
- Beijing Evergrow Resources ER-W-40G Polypropylene Super-Fine Filter Material
- PolyOne Synprene® IT 62-001 Thermoplastic Elastomer - SBC (discontinued **)
Copyright © lookpolymers.com All Rights Reserved