Techmer ES Elastoblend® PA6/6 IM 408 L Nylon 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Impact Grade |
| Manufacturer | Techmer ES |
| Trade Name | Elastoblend® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Techmer ES Elastoblend® PA6/6 IM 408 L Nylon 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Availability: North AmericaForms: PelletsAdditive: Lubricant and Impact ModifierFeatures: Lubricant and Impact ModifiedProcessing Method: Injection MoldingInformation provided by TP Composites, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.09 g/cc | 0.0394 lb/in³ | ASTM D792 |
| Water Absorption | 1.2 % @Time 86400 sec |
1.2 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.015 cm/cm @Thickness 3.17 mm |
0.015 in/in @Thickness 0.125 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 102 | 102 | ASTM D785 |
| Tensile Strength | 59.3 MPa | 8600 psi | ASTM D638 |
| Elongation at Break | 80 % | 80 % | ASTM D638 |
| Flexural Strength | 80.0 MPa | 11600 psi | ASTM D790 |
| Flexural Yield Strength | 82.7 MPa | 12000 psi | ASTM D790 |
| Flexural Modulus | 1.90 GPa | 275 ksi | ASTM D790 |
| Izod Impact, Notched | 0.534 J/cm @Thickness 3.17 mm, Temperature -40.0 °C |
1.00 ft-lb/in @Thickness 0.125 in, Temperature -40.0 °F |
ASTM D256 |
| 2.14 J/cm @Thickness 3.17 mm, Temperature 22.8 °C |
4.00 ft-lb/in @Thickness 0.125 in, Temperature 73.0 °F |
ASTM D256 | |
| Izod Impact, Unnotched | NB @Thickness 3.17 mm |
NB @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 79.2 µm/m-°C | 44.0 µin/in-°F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 224 °C | 435 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 71.1 °C | 160 °F | Unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 |
| Dielectric Strength | 17.3 kV/mm | 440 kV/in | Method A (Short-Time); ASTM D149 |
Users viewing this material also viewed the following:
- Owens Corning Glass Fiber Reinforced Polyester SMC (Compression), 22 wt.% glass
- Solvay Engineered Polymers DEXFLEX® 810HS TPO (discontinued **)
- Honeywell Aegis™ HCA95ZP Nylon 6/6,6 Extrusion Grade Copolymer (discontinued **)
- IRPC Polimaxx Polene 2500PC Polypropylene Block Copolymer
- Styron CALIBREâ„¢ IM 401-11 Polycarbonate Resin
- A. Schulman POLYBATCH™ Red LL50283/3 Concentrate Based In LLDPE
- CoorsTek PolyGlyde™ 2000 Self-Lubricating Seal
- Teknor Apex Sinvicomp DFR 5806 Polyvinyl Chloride, Rigid
- Solvay RHODICARE H Surfactant
Copyright © lookpolymers.com All Rights Reserved