- Acrylonitrile Butadiene Styrene (ABS), Impact Grade, Molded
- TPI Porene® ABS-GA850 High Impact ABS Resin
TPI Porene® ABS-GA850 High Impact ABS Resin
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Impact Grade, Molded |
| Manufacturer | Thai Petrochemical Industry Co. LTD. |
| Trade Name | Porene® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | TPI Porene® ABS-GA850 High Impact ABS Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by US distributor Polymer Technology and Services, LLC (PTS).
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.05 g/cc | 0.0379 lb/in³ | ASTM D792 |
| Melt Flow | 20 g/10 min @Load 10.0 kg, Temperature 220 °C |
20 g/10 min @Load 22.0 lb, Temperature 428 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 118 | 118 | ASTM D785 |
| Tensile Strength, Yield | 51.7 MPa @Thickness 3.17 mm |
7500 psi @Thickness 0.125 in |
|
| Flexural Yield Strength | 70.3 MPa @Thickness 3.17 mm |
10200 psi @Thickness 0.125 in |
|
| Flexural Modulus | 2.34 GPa @Thickness 3.17 mm |
339 ksi @Thickness 0.125 in |
|
| Izod Impact, Notched | 2.67 J/cm @Thickness 6.35 mm |
5.00 ft-lb/in @Thickness 0.250 in |
|
| 2.99 J/cm @Thickness 3.17 mm |
5.60 ft-lb/in @Thickness 0.125 in |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 96.0 °C | 205 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 87.0 °C | 189 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.59 mm |
HB @Thickness 0.0625 in |
|
| HB @Thickness 3.17 mm |
HB @Thickness 0.125 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 193 °C | 380 °F | |
| Middle Barrel Temperature | 216 °C | 420 °F | |
| Front Barrel Temperature | 232 °C | 450 °F | |
| Melt Temperature | 218 - 260 °C | 425 - 500 °F | Nozzle temp not greater than stock |
| Mold Temperature | 48.9 - 65.6 °C | 120 - 150 °F | |
| Drying Temperature | 87.8 - 93.3 °C | 190 - 200 °F | |
| Dry Time | 2 - 24 hour | 2 - 24 hour | |
| Injection Pressure | 68.9 - 82.7 MPa | 10000 - 12000 psi | |
| Back Pressure | 0.689 MPa | 100 psi | |
| Screw Speed | 50 - 60 rpm | 50 - 60 rpm |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Injection Fill Speed | Slow to Moderate |
Users viewing this material also viewed the following:
- Polystrand ThermoPro™ IE6021X ECR X-Ply Cross-Ply Polyethylene-Glass Composite
- Chevron Phillips 7109CLT LLDPE Blown Film Resin, Hexene Copolymer (discontinued **)
- LG Chemical Lupoy 1200HP-15 Polycarbonate Resin
- Special Metals Nickel 200
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 20 PHR N774 (SRF) Filler
- DSM Somos® 14120 Water-resistant resin for stereolithography, White
- EMS-Grivory Grivory® L 20 W 20 grey 9280 PA12
- ChevronTexaco RPM® SAE 15W-40 Heavy Duty Motor Oil
- 3M Scotch® 31 Heavy Duty Mining Tape
Copyright © lookpolymers.com All Rights Reserved