Suzhou Hipro Polymers Hiprolon® 70 MC HLS G30 Nylon 610, 30% glass fiber filled
| Category | Polymer , Renewable/Recycled Polymer , Thermoplastic , Nylon , Nylon 610 , Nylon 610, Glass Reinforced |
| Manufacturer | Suzhou Hipro Polymers |
| Trade Name | Hiprolon® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Suzhou Hipro Polymers Hiprolon® 70 MC HLS G30 Nylon 610, 30% glass fiber filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Hiprolon® 70 MC HLS G30 polyamide 6.10 compound reinforced with 30% chopped glass fiber for injection molding. Features: high heat resistance, dimension stability, impact resistance, good flow ability, and bio-renewable resource composition. Widely used for auto parts, electronics parts, thin- wall housing et al.Information provided by Suzhou Hipro Polymers Co. Ltd
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.31 g/cc | 0.0473 lb/in³ | ISO 1183 |
| Water Absorption | 0.80 % | 0.80 % | ISO 62 |
| Linear Mold Shrinkage | 0.0050 cm/cm | 0.0050 in/in | normal; ISO 294-4,2577 |
| Linear Mold Shrinkage, Flow | 0.010 cm/cm | 0.010 in/in | ISO 294-4,2577 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 150 MPa | 21800 psi | ISO 527-2/1A |
| Elongation at Break | 5.0 % | 5.0 % | ISO 527-2/1A |
| Tensile Modulus | 8.30 GPa | 1200 ksi | ISO 527-1/-2 |
| Charpy Impact Unnotched | 8.90 J/cm² @Temperature -30.0 °C |
42.4 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU |
| 9.00 J/cm² @Temperature 23.0 °C |
42.8 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 1.00 J/cm² @Temperature -30.0 °C |
4.76 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| 1.60 J/cm² @Temperature 23.0 °C |
7.61 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 222 °C | 432 °F | ISO 11357 |
| Deflection Temperature at 0.46 MPa (66 psi) | 221 °C | 430 °F | ISO 75-1/2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | ISO 75-1/2 |
| Vicat Softening Point | 217 °C | 423 °F | ISO 306 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
IEC60695 |
| HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ISO 60695 |
| Comparative Tracking Index | >= 600 V | >= 600 V | IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 260 - 300 °C | 500 - 572 °F | |
| Mold Temperature | 60.0 - 110 °C | 140 - 230 °F | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Dry Time | 4 hour | 4 hour | |
| Injection Pressure | 70.0 - 130 MPa | 10200 - 18900 psi |
Users viewing this material also viewed the following:
- 3M Scotch-Weld™ 3549 B/A Brown Two-Part Urethane Adhesive 3549 B/A Brown (discontinued **)
- Gouda Vuurvast LP 80 A Dense Refractory Brick
- Solvay TECHNYL® A 218 V15 PA66, 15% glass fiber, Conditioned
- SABIC Innovative Plastics PC1000 PC (Asia Pacific)
- SABIC Innovative Plastics LNP LUBRICOMP RI001 PA 66 (Europe-Africa-Middle East)
- Master Bond Mastersil 701 One Component, Room Temperature Curing Silicone Elastomer
- DSM Novamid® 2030A PA666
- Equate EFDC-7087 LLDPE Film Extrusion Resin
- BASF Elastollan R 1000 20% Glass Filled TPUR
- Potters Industries Spheriglass® 3000E Solid Glass Spheres
Copyright © lookpolymers.com All Rights Reserved