SABIC Innovative Plastics Noryl GTX GTX966 PPE+PA66 (Asia Pacific)

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Polyphenylene Ether/PPO
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name NORYL GTX
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Noryl GTX GTX966 PPE+PA66 (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
>PPE+PA66-I-TD10
Physical Properties Metric English Comments
Specific Gravity 1.16 g/cc
1.16 g/cc
ASTM D 792
Density 1.17 g/cc
0.0423 lb/in³
ISO 1183
Moisture Absorption at Equilibrium 1.1 %
1.1 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 3.8 %

@Temperature 23.0 °C
 3.8 %

@Temperature 73.4 °F
 ISO 62
Linear Mold Shrinkage, Flow 0.010 - 0.012 cm/cm
0.010 - 0.012 in/in
on tensile bar; SABIC Method
0.010 - 0.012 cm/cm

@Thickness 3.20 mm
 0.010 - 0.012 in/in

@Thickness 0.126 in
 SABIC Method
Linear Mold Shrinkage, Transverse 0.0090 - 0.011 cm/cm

@Thickness 3.20 mm
 0.0090 - 0.011 in/in

@Thickness 0.126 in
 SABIC Method
Melt Flow 15 g/10 min

@Load 5.00 kg,
Temperature 280 °C
 15 g/10 min

@Load 11.0 lb,
Temperature 536 °F
 ASTM D 1238
20 g/10 min

@Load 5.00 kg,
Temperature 280 °C
 20 g/10 min

@Load 11.0 lb,
Temperature 536 °F
 [cm^3/10 min] Melt Volume Rate; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 60.0 MPa
8700 psi
Type I, 5 mm/min; ASTM D 638
60.0 MPa
8700 psi
50 mm/min; ISO 527
Tensile Strength, Yield 65.0 MPa
9430 psi
Type I, 5 mm/min; ASTM D 638
65.0 MPa
9430 psi
50 mm/min; ISO 527
Elongation at Break 20 %
20 %
50 mm/min; ISO 527
40 %
40 %
Type I, 5 mm/min; ASTM D 638
Elongation at Yield 4.5 %
4.5 %
Type I, 5 mm/min; ASTM D 638
4.5 %
4.5 %
50 mm/min; ISO 527
Tensile Modulus 3.00 GPa
435 ksi
5 mm/min; ASTM D 638
3.10 GPa
450 ksi
1 mm/min; ISO 527
Flexural Yield Strength 90.0 MPa
13100 psi
2 mm/min; ISO 178
100 MPa
14500 psi
1.3 mm/min, 50 mm span; ASTM D 790
Flexural Modulus 2.90 GPa
421 ksi
2 mm/min; ISO 178
2.95 GPa
428 ksi
1.3 mm/min, 50 mm span; ASTM D 790
Izod Impact, Notched 0.600 J/cm

@Temperature 23.0 °C
 1.12 ft-lb/in

@Temperature 73.4 °F
 ASTM D 256
0.600 J/cm

@Temperature -30.0 °C
 1.12 ft-lb/in

@Temperature -22.0 °F
 ASTM D 256
Izod Impact, Notched (ISO) 5.00 kJ/m²

@Temperature -30.0 °C
 2.38 ft-lb/in²

@Temperature -22.0 °F
 80*10*4; ISO 180/1A
7.00 kJ/m²

@Temperature 23.0 °C
 3.33 ft-lb/in²

@Temperature 73.4 °F
 80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) NB

@Temperature 23.0 °C
 NB

@Temperature 73.4 °F
 80*10*4; ISO 180/1U
Charpy Impact, Notched 0.800 J/cm²

@Temperature 23.0 °C
 3.81 ft-lb/in²

@Temperature 73.4 °F
 V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA
Impact Test 25.0 J

@Temperature 23.0 °C
 18.4 ft-lb

@Temperature 73.4 °F
 Instrumented Impact Total Energy; ASTM D 3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 70.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
 38.9 µin/in-°F

@Temperature 73.4 - 140 °F
 ISO 11359-2
71.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 39.4 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
CTE, linear, Transverse to Flow 75.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
 41.7 µin/in-°F

@Temperature 73.4 - 140 °F
 ISO 11359-2
79.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 43.9 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
Deflection Temperature at 0.46 MPa (66 psi) 190 °C
374 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
190 °C

@Thickness 3.20 mm
 374 °F

@Thickness 0.126 in
 unannealed; ASTM D 648
Vicat Softening Point 195 °C
383 °F
Rate B/50; ISO 306
200 °C
392 °F
Rate B/120; ISO 306
200 °C
392 °F
Rate B/50; ASTM D 1525