- Arlon Thermabond® 99950N015 Silicone Rubber/Fiberglass Laminate
Arlon Thermabond® 99950N015 Silicone Rubber/Fiberglass Laminate
| Category | Polymer , Adhesive , Thermoset , Rubber or Thermoset Elastomer (TSE) , Silicone , Silicone Rubber |
| Manufacturer | Arlon |
| Trade Name | Thermabond® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Arlon Thermabond® 99950N015 Silicone Rubber/Fiberglass Laminate.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Electrically conductive, Thermabond®. primerless. Liner: 1 mil FEP; Product: uncured silicone rubber; Carrier: 3 mil PTFE coated fiberglass.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 3.70 g/cc | 3.70 g/cc | silicone property; Arlon SQA-TMS-024 |
| Thickness | 381 microns | 15.0 mil | overall; Arlon SQA-TMS-003 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 84 | 84 | silicone property; ASTM D2240 |
| Tensile Strength, Ultimate | 3.34 MPa | 485 psi | silicone property; ASTM D412 |
| Elongation at Break | 60 % | 60 % | silicone property; ASTM D412 |
| Modulus of Elasticity | 0.01957 GPa | 2.838 ksi | silicone property; Arlon SQA-TMS-008 |
| Poissons Ratio | 0.50 | 0.50 | silicone property |
| Shear Modulus | 0.379 GPa | 55.0 ksi | silicone property; ASTM D1002 |
| Shear Strength | 3.65 MPa | 530 psi | silicone property; ASTM D1002 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 93.0 µm/m-°C @Temperature 20.0 °C |
51.7 µin/in-°F @Temperature 68.0 °F |
silicone property; ASTM E 831 |
| Specific Heat Capacity | 0.400 J/g-°C | 0.0956 BTU/lb-°F | silicone property; ASTM E 1461-1 |
| Thermal Conductivity | 2.50 W/m-K | 17.4 BTU-in/hr-ft²-°F | silicone property; ASTM E 1530 |
| Maximum Service Temperature, Air | 204 °C | 400 °F | |
| Minimum Service Temperature, Air | -73.3 °C | -100 °F | |
| Glass Transition Temp, Tg | -116 °C | -177 °F | silicone property; ASTM E 1356 |
| Flammability, UL94 | V-0 | V-0 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 0.050 ohm-cm | 0.050 ohm-cm | silicone property; ASTM D991 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Cure Time | 15.0 min @Temperature 141 °C |
0.250 hour @Temperature 285 °F |
|
| Shelf Life | 6.00 Month @Temperature 7.22 °C |
6.00 Month @Temperature 45.0 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Naturally Gray |
Users viewing this material also viewed the following:
- Nilit Nilitop BT G6 General Purpose, 30% Glass Fiber Reinforced PBT
- Lanxess Pocan® B 1505 Z 000000 PBT
- Shinkong Synthetic Fibers Shinite® PP4220 PP, High Impact, Fire Retardant
- Taiwan Sheen Soon Sheenthane® AH-530 TPU for Hotmelt Adhesive
- Chevron Phillips MarFlex® D143 m-LLDPE Linear Low Density Polyethylene
- 3M Scotchcal™ 50-84 Graphic Film
- Polimeri Europa Extir® D 5000 AE Expandable Polystyrene - Flame Retardant
- DuPont Performance Polymers Hypalon® 40S Chlorosulfonated Polyethylene Rubber, Peroxide Cured Carbon Black Filled Compound
- BASF Ultramid® B3WG5 25% Glass Filled PA6 (Conditioned)
Copyright © lookpolymers.com All Rights Reserved