SABIC Innovative Plastics LNP STAT-KON TE002 PU
| Category | Polymer , Thermoplastic , Polyurethane, TP |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-KON TE002 PU.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* STAT-KON* TE002 is a compound based on Polyurethane resin containing 10% Carbon Fiber. Added feature of this material is: Electrically Conductive.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.27 g/cc | 0.0459 lb/in³ | ASTM D792 |
| 1.27 g/cc | 0.0459 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.460 % | 0.460 % | 50% RH, 24 hrs; ASTM D570 |
| 0.600 % | 0.600 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm @Time 86400 sec |
0.0010 - 0.0030 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0020 - 0.0040 cm/cm @Time 86400 sec |
0.0020 - 0.0040 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 48.0 MPa | 6960 psi | Type I, 5 mm/min; ASTM D638 |
| 49.0 MPa | 7110 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 50.0 MPa | 7250 psi | 5 mm/min; ISO 527 |
| 52.0 MPa | 7540 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 19.8 % | 19.8 % | 5 mm/min; ISO 527 |
| 22.8 % | 22.8 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 15.7 % | 15.7 % | 5 mm/min; ISO 527 |
| 19.2 % | 19.2 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 1.30 GPa | 189 ksi | 50 mm/min; ASTM D638 |
| 1.58 GPa | 229 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 51.0 MPa | 7400 psi | ISO 178 |
| Flexural Modulus | 1.16 GPa | 168 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 1.66 GPa | 241 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 4.78 J/cm | 8.95 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 16.89 J/cm | 31.64 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 37.0 kJ/m² | 17.6 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 128 kJ/m² | 60.9 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 23.0 J @Temperature 23.0 °C |
17.0 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 15.0 J | 11.1 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 1.00 µm/m-°C @Temperature -30.0 - 30.0 °C |
0.556 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 16.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
8.89 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 175 °C | 347 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 141 °C @Thickness 3.20 mm |
286 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 88.0 °C | 190 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 82.0 °C @Thickness 3.20 mm |
180 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 5.0 - 8.0 ohm | 5.0 - 8.0 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- Polykemi AB POLYblend 6005 PC/ABS-Blend
- SABIC Innovative Plastics Lexan® LUX2114G PC (Asia Pacific)
- SABIC Innovative Plastics LNP STAT-KON DEF42 PC
- Techmer ES HiFill® PA6/6 GB30 L 30% Glass Bead Filler
- CP-Polymer-Technik Wellamid® 6600 MZ 401 CP Combination Nylon 66, Conditioned
- Dymax 3-3073 Flexible Potting
- AK Steel ASTM A 907, Grade 30 Hot Rolled Carbon Steel, Structural Quality (SQ)
- DuPont Elvax® PE3507-2 Ethylene Vinyl Acetate (discontinued **)
Copyright © lookpolymers.com All Rights Reserved