- Styron Pulse® 830 ABS + Polycarbonate
Styron Pulse® 830 ABS + Polycarbonate
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC) |
| Manufacturer | Styron |
| Trade Name | Pulse® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Styron Pulse® 830 ABS + Polycarbonate.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PULSE® 830 Engineering resin offers excellent processability, high heat resistance, and high impact strength at both room and low temperatures.PULSE 830 Engineering resin has been used in automotive instrument panel and interior trim applications.Data provided by Dow Chemical.This product line was spun off from Dow Chemical to Styron in 2010.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in³ | ASTM Data |
| Melt Density | 0.962 g/cc | 0.0348 lb/in³ | Melt density |
| Water Absorption | 0.15 % | 0.15 % | |
| Moisture Absorption at Equilibrium | 0.32 % | 0.32 % | Humidity Absorption |
| Linear Mold Shrinkage | 0.0070 cm/cm | 0.0070 in/in | |
| Melt Flow | 3.0 g/10 min @Load 3.80 kg, Temperature 230 °C |
3.0 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM Data |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 115 | 115 | |
| Tensile Strength, Ultimate | 44.8 MPa | 6500 psi | ASTM Data |
| Tensile Strength, Yield | 53.1 MPa | 7700 psi | ASTM Data |
| Elongation at Break | 125 % | 125 % | ASTM Data |
| Elongation at Yield | 4.0 % | 4.0 % | ISO Data |
| Tensile Modulus | 2.30 GPa | 334 ksi | ISO Data. |
| Izod Impact, Notched | 6.41 J/cm | 12.0 ft-lb/in | ASTM Data |
| 5.34 J/cm @Temperature -50.0 °C |
10.0 ft-lb/in @Temperature -58.0 °F |
ASTM Data | |
| Charpy Impact Unnotched | NB | NB | ISO Data |
| NB | NB | ISO Data, Low Temp | |
| Charpy Impact, Notched | 2.50 J/cm² | 11.9 ft-lb/in² | ISO Data, Low Temp |
| 6.60 J/cm² | 31.4 ft-lb/in² | ISO Data | |
| Impact Test | 56.5 J @Temperature 23.0 °C |
41.7 ft-lb @Temperature 73.4 °F |
Instrumented Dart Total Energy |
| 62.2 J @Temperature -30.0 °C |
45.9 ft-lb @Temperature -22.0 °F |
Instrumented Dart Total Energy |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 73.8 µm/m-°C @Temperature 20.0 °C |
41.0 µin/in-°F @Temperature 68.0 °F |
ASTM data |
| Specific Heat Capacity | 1.93 J/g-°C | 0.461 BTU/lb-°F | |
| Thermal Conductivity | 0.160 W/m-K | 1.11 BTU-in/hr-ft²-°F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 110 °C | 230 °F | Unannealed; ASTM Data |
| 121 °C | 250 °F | annealed; ASTM Data |
Users viewing this material also viewed the following:
- Chevron Phillips Vytek™ V208C3 Enhanced LLDPE Blown Film Resin (discontinued **)
- Overview of materials for Phenolic, Carbon Fiber Composite
- Lehmann & Voss LUVOCOM® 19-7748 Polyamide 46, with carbon fiber, PTFE, lubricant modified
- Haynes R-41 alloy, 1.27 mm thick sheet, solution heat treated at 1079°C, water quenched, 30 minutes at 1066°C, aged 16 hours at 760°C (1400°F), air cooled
- Special Metals INCONEL® 686 Nickel Superalloy (UNS N06686) Plate 0.500 in (12.7 mm)
- UBE UBEPOL BR15H HIPS (n-DM = 0.03 wt % and PH-3H = 0.03 wt %)
- Chesterton ARC 890 Course Grade Sliding Wear Compound
- ChevronTexaco HPLX SAE 30 Chevron HPLX Low Ash Gas Engine Oil
- DAK Americas Laser+® HS CF746A (D53A) PET
Copyright © lookpolymers.com All Rights Reserved