- Acrylonitrile Butadiene Styrene (ABS), 10% Glass Fiber Filled
- Aclo Accutech ABS ABS833G10L Glass Reinforced
Aclo Accutech ABS ABS833G10L Glass Reinforced
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), 10% Glass Fiber Filled |
| Manufacturer | Aclo Compounders |
| Trade Name | Accutech |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Aclo Accutech ABS ABS833G10L Glass Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.10 g/cc | 0.0397 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0020 cm/cm | 0.0020 in/in | MD; ASTM D955 |
| Melt Flow | 1.4 g/10 min | 1.4 g/10 min | ASTM D1238 |
| Ash | 10 % | 10 % | ASTM D2584 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 110 | 110 | ASTM D785 |
| Tensile Strength at Break | 63.0 MPa | 9140 psi | ASTM D638 |
| Tensile Strength, Yield | 63.0 MPa | 9140 psi | ASTM D638 |
| Elongation at Break | 5.0 % | 5.0 % | ASTM D638 |
| Elongation at Yield | 4.0 % | 4.0 % | ASTM D638 |
| Tensile Modulus | 3.00 GPa | 435 ksi | ASTM D638 |
| Flexural Strength | 95.01 MPa | 13780 psi | ASTM D790 |
| Flexural Modulus | 3.900 GPa | 565.6 ksi | ASTM D790 |
| Izod Impact, Notched | 0.747 J/cm | 1.40 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 97.8 °C | 208 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 87.2 °C | 189 °F |
Users viewing this material also viewed the following:
- Plastcom SLOVALEN PC 51 C 20 PP, 20% mineral filling
- Rogers Corporation RO3210 Woven-Glass Reinforced PTFE Laminate
- 3M Dyneon™ PFA 6505N Perfluoroalkoxy Fluorothermoplastic (discontinued **)
- Lehmann & Voss LUVOCOM® 1105-8529 PEEK, with carbon fiber
- Menzolit Menzolit® SMC 2400 Unsaturated Polyester UP
- Lotte Chemical Titan TITANLENE® LDF264YZ Low density polyethylene
- Techmer ES HiFill® PA4/6 GF33 HS NAT 33% Glass Filled (Conditioned)
- Zircar Zirconia Buster Blanket Alumina Blanket Insulation
- Dow Engage® 8411 Polyolefin Elastomer
- Arkema Group OREVAC® 18750 Maleic Anhydride Modified Polypropylene
Copyright © lookpolymers.com All Rights Reserved