SABIC Innovative Plastics LNP STAT-LOY A3000T ABS
| Category | Polymer , Thermoplastic , ABS Polymer |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP Stat-loy |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-LOY A3000T ABS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* STAT-LOY A3000T is a compound based on ABS. Added features of this grade include: Antistatic, Clear.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.08 g/cc | 1.08 g/cc | ASTM D792 |
| Density | 1.08 g/cc | 0.0390 lb/in³ | ASTM D792 |
| 1.08 g/cc | 0.0390 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.800 % | 0.800 % | 50% RH, 24 hrs; ASTM D570 |
| 0.800 % | 0.800 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Time 86400 sec |
0.0050 - 0.0070 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0068 cm/cm @Time 86400 sec |
0.0068 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0070 - 0.0090 cm/cm @Time 86400 sec |
0.0070 - 0.0090 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0083 cm/cm @Time 86400 sec |
0.0083 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 24.0 MPa | 3480 psi | Type I, 5 mm/min; ASTM D638 |
| 24.0 MPa | 3480 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 32.0 MPa | 4640 psi | Type I, 5 mm/min; ASTM D638 |
| 32.0 MPa | 4640 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 39 % | 39 % | Type I, 5 mm/min; ASTM D638 |
| 62.9 % | 62.9 % | ISO 527 | |
| 63 % | 63 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 1.14 GPa | 165 ksi | 1 mm/min; ISO 527 |
| 1.21 GPa | 175 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 42.0 MPa | 6090 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 42.0 MPa | 6090 psi | ISO 178 | |
| Flexural Modulus | 1.41 GPa | 205 ksi | 2 mm/min; ISO 178 |
| 1.47 GPa | 213 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 1.33 J/cm | 2.49 ft-lb/in | ASTM D256 |
| Izod Impact, Notched (ISO) | 11.0 kJ/m² | 5.23 ft-lb/in² | 80*10*4; ISO 180/1A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 118 µm/m-°C @Temperature -40.0 - 40.0 °C |
65.6 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 119 µm/m-°C @Temperature -40.0 - 40.0 °C |
66.1 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| CTE, linear, Transverse to Flow | 112 µm/m-°C @Temperature -40.0 - 40.0 °C |
62.2 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 112 µm/m-°C @Temperature -40.0 - 40.0 °C |
62.2 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 81.0 °C | 178 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 81.0 °C @Thickness 3.20 mm |
178 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 68.0 °C | 154 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 87.0 °C @Thickness 3.20 mm |
189 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 9.0 - 11 ohm-cm | 9.0 - 11 ohm-cm | ASTM D257 |
| Surface Resistance | 1.00e+10 - 1.00e+12 ohm | 1.00e+10 - 1.00e+12 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- Palm Labs Adhesives Turbo Fuse Series 150 (500 Viscosity) Rapid Bonding Adhesive
- Pyrotek G-2 Low-Temperature Felt
- Radici Radilon® A RCF3505 (dry) Nylon 66
- PolyOne Elastamax™ EG-9177 Thermoplastic Elastomer (TPE)
- Nitriflex N-7 NBR - Nitrile Rubber
- SABIC Innovative Plastics LNP STAT-KON WE002 PBT
- Polyram PlusTek PA841 Nylon 6.6, Impact Modified
- Wellman EcoLon® MRGF1616-BK 40% Mineral/Glass Reinforced Post Consumer Compound Nylon 6
Copyright © lookpolymers.com All Rights Reserved