Material Notes:
Overview: MAGNUM™ 3904 is an extrusion/thermoforming resin developed for high impact and other technical applications. The mass (continuous process) ABS technology of Styron ensures an ABS technology of Styron ensures an ABS resin that combines excellent processabiltiy with a stable light base color that is ideal for self-coloring. The new MAGNUM ‘Smooth Series’ resins have an ultra low particulate content, which results in a good surface finish that will enable our customers to produce parts with excellent aesthetics at a low total cost.Applications: TransportationProtective coversSanitary wareMarineSignageRecreation vehiclesFurnishingsInformation provided by Styron
Physical Properties Metric English Comments
Density 1.05 g/cc
0.0379 lb/in³
ISO 1183/B
Apparent Bulk Density 0.650 g/cc
0.0235 lb/in³
ISO 60
Linear Mold Shrinkage, Flow 0.0040 - 0.0070 cm/cm
0.0040 - 0.0070 in/in
ISO 294-4
Melt Flow 4.7 g/10 min

@Load 10.0 kg,
Temperature 220 °C
 4.7 g/10 min

@Load 22.0 lb,
Temperature 428 °F
 ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength, Yield 37.0 MPa

@Thickness 3.20 mm
 5370 psi

@Thickness 0.126 in
 Injection Molded; ISO 527-2/50
39.0 MPa

@Thickness 3.20 mm
 5660 psi

@Thickness 0.126 in
 Injection Molded; ISO 527-2/100
Elongation at Yield 2.6 %

@Thickness 3.20 mm
 2.6 %

@Thickness 0.126 in
 Injection Molded; ISO 527-2/50
2.8 %

@Thickness 3.20 mm
 2.8 %

@Thickness 0.126 in
 Injection Molded; ISO 527-2/100
Tensile Modulus 1.82 GPa

@Thickness 3.20 mm
 264 ksi

@Thickness 0.126 in
 Injection Molded; ISO 527-2
Flexural Strength 58.0 MPa

@Thickness 3.20 mm
 8410 psi

@Thickness 0.126 in
 3-points, 2 mm/min, Injection Molded; ISO 178
Flexural Modulus 1.90 GPa

@Thickness 3.20 mm
 276 ksi

@Thickness 0.126 in
 3-points, 2 mm/min, Injection Molded; ISO 178
Izod Impact, Notched (ISO) 17.0 kJ/m²

@Temperature -30.0 °C
 8.09 ft-lb/in²

@Temperature -22.0 °F
 Injection Molded; ISO 180/A
42.0 kJ/m²

@Temperature 23.0 °C
 20.0 ft-lb/in²

@Temperature 73.4 °F
 Injection Molded; ISO 180/A
Charpy Impact, Notched 1.20 J/cm²

@Temperature -30.0 °C
 5.71 ft-lb/in²

@Temperature -22.0 °F
 Injection Molded; ISO 179/2C
1.80 J/cm²

@Temperature -30.0 °C
 8.57 ft-lb/in²

@Temperature -22.0 °F
 Injection Molded; ISO 179/1eA
2.20 J/cm²

@Temperature 23.0 °C
 10.5 ft-lb/in²

@Temperature 73.4 °F
 Injection Molded; ISO 179/2
3.70 J/cm²

@Temperature 23.0 °C
 17.6 ft-lb/in²

@Temperature 73.4 °F
 Injection Molded; ISO 179/1eA
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 97.0 °C
207 °F
Annealed; ISO 75-2/A
Vicat Softening Point 97.0 °C
207 °F
ISO 306/B50
Flammability, UL94 HB

@Thickness 1.50 mm
 HB

@Thickness 0.0591 in
HB

@Thickness 3.00 mm
 HB

@Thickness 0.118 in
Flame Spread 40.0 mm/min
1.57 in/min
ISO 3795