Seals Eastern 7182A Fluorocarbon-Elastomer

Category Polymer , Thermoset , Fluoropolymer, TS , Thermoset Fluoroelastomer , Rubber or Thermoset Elastomer (TSE)
Manufacturer Seals Eastern, Inc
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Seals Eastern 7182A Fluorocarbon-Elastomer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Formulated AFLAS® high-temperature, high-pressure "sour" oil & gas service. Resistant to extrusion. Excellent acid and base resistance.Information provided by Seals Eastern, Inc.
Physical Properties Metric English Comments
Specific Gravity 1.59 g/cc
1.59 g/cc
ASTM D297, 15
Mechanical Properties Metric English Comments
Hardness, Shore A >= 93
>= 93
ASTM D2240, Type A
96
96
AVG; ASTM D2240, Type A
93

@Temperature 200 °C,
Time 252000 sec
 93

@Temperature 392 °F,
Time 70.0 hour
 After Dry Heat Aging; ASTM D865
98

@Temperature 200 °C,
Time 1.21e+6 sec
 98

@Temperature 392 °F,
Time 336 hour
 After Dry Heat Aging; ASTM D865
98

@Temperature 200 °C,
Time 3.60e+6 sec
 98

@Temperature 392 °F,
Time 1000 hour
 After Dry Heat Aging; ASTM D865
Tensile Strength at Break >= 15.9 MPa
>= 2300 psi
ASTM D412 Method A
20.0 MPa
2900 psi
AVG; ASTM D412 Method A
19.00 MPa

@Temperature 200 °C,
Time 252000 sec
 2755 psi

@Temperature 392 °F,
Time 70.0 hour
 After Dry Heat Aging; ASTM D865
24.99 MPa

@Temperature 200 °C,
Time 3.60e+6 sec
 3625 psi

@Temperature 392 °F,
Time 1000 hour
 After Dry Heat Aging; ASTM D865
25.79 MPa

@Temperature 200 °C,
Time 1.21e+6 sec
 3741 psi

@Temperature 392 °F,
Time 336 hour
 After Dry Heat Aging; ASTM D865
Tensile Strength, Yield >= 9.205 MPa
>= 1335 psi
Stress at Elongation M100; ASTM D412 Method A
12.56 MPa
1822 psi
AVG Stress at Elongation M25; ASTM D412 Method A
>= 13.4 MPa
>= 1950 psi
Stress at Elongation M50; ASTM D412 Method A
14.66 MPa
2126 psi
AVG Stress at Elongation M50; ASTM D412 Method A
18.38 MPa
2666 psi
AVG Stress at Elongation M100; ASTM D412 Method A
Elongation at Break >= 60 %
>= 60 %
ASTM D412 Method A
75 %
75 %
AVG; ASTM D412 Method A
74.3 %

@Temperature 200 °C,
Time 252000 sec
 74.3 %

@Temperature 392 °F,
Time 70.0 hour
 After Dry Heat Aging; ASTM D865
82.5 %

@Temperature 200 °C,
Time 3.60e+6 sec
 82.5 %

@Temperature 392 °F,
Time 1000 hour
 After Dry Heat Aging; ASTM D865
84 %

@Temperature 200 °C,
Time 1.21e+6 sec
 84 %

@Temperature 392 °F,
Time 336 hour
 After Dry Heat Aging; ASTM D865
Tear Strength Test 323
323
(psi); ASTM D624, Die B
Compression Set 32 %

@Temperature 200 °C,
Time 79200 sec
 32 %

@Temperature 392 °F,
Time 22.0 hour
 ASTM D395, Test B
47 %

@Temperature 200 °C,
Time 252000 sec
 47 %

@Temperature 392 °F,
Time 70.0 hour
 ASTM D395, Test B
Thermal Properties Metric English Comments
Glass Transition Temp, Tg 2.78 °C
37.0 °F
ASTM D1329
Processing Properties Metric English Comments
Shelf Life 240 Month
240 Month
ASTM D395, Test B
Descriptive Properties Value Comments
Strain Energy / Unit Volume at 20% Elongation (psi) 283