Styron EMERGEâ„¢ 4600-10 Polycarbonate
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | Styron |
| Trade Name | EMERGE™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Styron EMERGEâ„¢ 4600-10 Polycarbonate.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
EMERGEâ„¢ PC 4600-10 advanced resin is formulated to supply both clarity and enhanced ignition resistance while maintaining excellent physical properties. Applications: Information Technology Equipment Sockets, Plugs, and Switches Street Lights, Safety Lights, and Reflectors Information provided by DowThis product line was spun off from Dow Chemical to Styron in 2010.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | ASTM D955 |
| Melt Flow | 10 g/10 min @Load 1.20 kg, Temperature 300 °C |
10 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 123 | 123 | ASTM D785 |
| Tensile Strength, Ultimate | 65.5 MPa | 9500 psi | ASTM D638 |
| Tensile Strength, Yield | 60.7 MPa | 8800 psi | ASTM D638 |
| Elongation at Break | 120 % | 120 % | ASTM D638 |
| Elongation at Yield | 6.0 % | 6.0 % | ASTM D638 |
| Tensile Modulus | 2.24 GPa | 325 ksi | ASTM D638 |
| Flexural Strength | 100 MPa | 14500 psi | ASTM D790 |
| Flexural Modulus | 2.41 GPa | 350 ksi | ASTM D790 |
| Izod Impact, Notched | 8.76 J/cm | 16.4 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | NB | NB | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 68.4 µm/m-°C @Temperature -40.0 - 82.2 °C |
38.0 µin/in-°F @Temperature -40.0 - 180 °F |
ASTM D696 |
| Hot Ball Pressure Test | >= 125 °C | >= 257 °F | IEC 60335-1 |
| Deflection Temperature at 0.46 MPa (66 psi) | 144 °C | 291 °F | annealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 127 °C | 260 °F | unannealed; ASTM D648 |
| 140 °C | 284 °F | annealed; ASTM D648 | |
| Vicat Softening Point | 154 °C | 309 °F | 50°C/hr, 50N; ASTM D1525 |
| UL RTI, Electrical | 125 °C | 257 °F | UL 746 |
| UL RTI, Mechanical with Impact | 110 °C | 230 °F | UL 746 |
| UL RTI, Mechanical without Impact | 125 °C | 257 °F | UL 746 |
| Flammability, UL94 | V-2 | V-2 | 0.0625 in |
| V-0 | V-0 | 0.125 in | |
| Oxygen Index | 41 % | 41 % | ASTM D2863 |
| Glow Wire Test | 960 °C @Thickness 2.00 mm |
1760 °F @Thickness 0.0787 in |
IEC 60695-2-10 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Transmission, Visible | 84 - 88 % | 84 - 88 % | ASTM D1003 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 3.0 @Frequency 100 - 1.00e+6 Hz |
3.0 @Frequency 100 - 1.00e+6 Hz |
ASTM D150 |
| Dielectric Strength | 16.7 kV/mm | 425 kV/in | ASTM D149 |
| Dissipation Factor | 0.0010 @Frequency 100 Hz |
0.0010 @Frequency 100 Hz |
ASTM D150 |
| 0.0040 @Frequency 1e+6 Hz |
0.0040 @Frequency 1e+6 Hz |
ASTM D150 | |
| Comparative Tracking Index | 250 V @Thickness 2.00 mm |
250 V @Thickness 0.0787 in |
IEC 60112 |
Users viewing this material also viewed the following:
- NOVA Chemicals Sclair® 11L1 Octene LLDPE Film Resin (discontinued **)
- Polimeri Europa KOBLEND PCA PD 935 G4 PC+ABS, 20% Glass Fiber (discontinued **)
- Lord Adhesives 19B Mix-In Black Accelerator for 200, 400, 500 Series
- Techmer ES HiFill® TPX-HTN-01033 A 40% Glass Filled
- Borealis FT3200 Low Density Polyethylene
- TIMET TIMETAL® 6-4 ELI Titanium Alloy (Ti-6Al-4V ELI; ASTM Grade 23) (Annealed;
- Dow ELITE™ 5401G Enhanced Polyethylene Resin
- Dow DOWLEX™ 2021D Linear Low Density Polyethylene
- BCC Products BC 6004 Epoxy Surface Coat
- DuPont Performance Polymers Zytel® 73G15L NC010 Nylon 6 (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved