Styron CALIBREâ„¢ 301-6 Polycarbonate Resin
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | Styron |
| Trade Name | CALIBRE™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Styron CALIBREâ„¢ 301-6 Polycarbonate Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Overview: CALIBREâ„¢ 300-6 polycarbonate resins offer exceptional impact resistance, heat distortion resistance and optical clarity as well as high melt strength for blow molding and sheet applications. The CALIBREâ„¢ 300-6 series products are available in 4 additive packages: CALIBREâ„¢ 300: No mold release or UV Stabilizer. CALIBREâ„¢ 301: Mold release. CALIBREâ„¢ 302: UV stabilizer. CALIBREâ„¢ 303: Mold release and UV stabilizer.Applications:Automotive interiorsAutomotive exteriorsSheet applicationsElectrical lighting/switchesSmall & large appliancesBeverage containers/servicewarePower equipmentGovt. and Industry Standards:CSAUnderwriters Laboratory (UL) Information provided by Styron
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in³ | ISO 1183/A |
| Water Absorption | 0.32 % @Temperature 23.0 °C |
0.32 % @Temperature 73.4 °F |
Equilibrium, 50% RH; ISO 62 |
| 0.15 % @Temperature 23.0 °C, Time 86400 sec |
0.15 % @Temperature 73.4 °F, Time 24.0 hour |
ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | ISO 294-4 |
| Melt Flow | 6.0 g/10 min @Load 1.20 kg, Temperature 300 °C |
6.0 g/10 min @Load 2.65 lb, Temperature 572 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 73 | 73 | ASTM D785 |
| Hardness, Rockwell R | 118 | 118 | ASTM D785 |
| Tensile Strength at Break | 72.0 MPa | 10400 psi | ISO 527-2/50 |
| 72.4 MPa | 10500 psi | 50 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 60.0 MPa | 8700 psi | 50 mm/min; ASTM D638; ISO 527-2/50 |
| Elongation at Break | 150 % | 150 % | 50 mm/min; ASTM D638 |
| Elongation at Yield | 6.0 % | 6.0 % | 50 mm/min; ASTM D638; ISO 527-2/50 |
| Tensile Modulus | 2.30 GPa | 334 ksi | ISO 527-2/50 |
| 2.41 GPa | 350 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 96.5 MPa | 14000 psi | Method I (3 point load), 2.0 mm/min; ASTM D790 |
| 97.0 MPa | 14100 psi | 2.0 mm/min; ISO 178 | |
| Flexural Modulus | 2.40 GPa | 348 ksi | 2.0 mm/min; ISO 178 |
| 2.41 GPa | 350 ksi | Method I (3 point load), 2.0 mm/min; ASTM D790 | |
| Izod Impact, Notched | 9.10 J/cm @Temperature 23.0 °C |
17.0 ft-lb/in @Temperature 73.4 °F |
ASTM D256 |
| Izod Impact, Notched (ISO) | 93.0 kJ/m² @Temperature 23.0 °C |
44.3 ft-lb/in² @Temperature 73.4 °F |
ISO 180/4A |
| Izod Impact, Unnotched (ISO) | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ISO 180; ASTM D256A |
| Charpy Impact, Notched | 5.50 J/cm² @Temperature 23.0 °C |
26.2 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Tensile Impact Strength | 588 kJ/m² | 280 ft-lb/in² | ASTM D1822 |
| Dart Drop, Total Energy | 90.4 J | 66.7 ft-lb | 3.39 m/sec; ASTM D3763 |
| Abrasion | 45 | 45 | [%] Taber; ASTM D1004 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 68.0 µm/m-°C @Temperature -40.0 - 82.0 °C |
37.8 µin/in-°F @Temperature -40.0 - 180 °F |
ASTM D696 |
| Hot Ball Pressure Test | 125 °C | 257 °F | IEC 60335-1 |
| Deflection Temperature at 0.46 MPa (66 psi) | 145 °C | 293 °F | Annealed; ASTM D648 |
| 146 °C | 295 °F | Annealed; ISO 75-2/B | |
| Deflection Temperature at 1.8 MPa (264 psi) | 126 °C | 259 °F | Unannealed; ISO 75-2/A |
| 129 °C | 264 °F | Unannealed; ASTM D648 | |
| 142 °C | 288 °F | Annealed; ASTM D648 | |
| 143 °C | 289 °F | Annealed; ISO 75-2/A | |
| Vicat Softening Point | 151 °C @Load 5.10 kg |
304 °F @Load 11.2 lb |
Rate A (50°C/h); ASTM D1525; ISO 360/B50 |
| Flammability, UL94 | HB @Thickness 1.59 mm |
HB @Thickness 0.0626 in |
|
| HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
||
| Oxygen Index | 26 % | 26 % | ISO 4289-2 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Refractive Index | 1.586 | 1.586 | ASTM D542; ISO 489 |
| Haze | 1.0 % | 1.0 % | ASTM D1003 |
| Transmission, Visible | 89 % | 89 % | ASTM D1003 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 2.00e+17 ohm-cm | 2.00e+17 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.0 @Frequency 60.0 Hz |
3.0 @Frequency 60.0 Hz |
ASTM D150 |
| 3.0 @Frequency 1.00e+6 Hz |
3.0 @Frequency 1.00e+6 Hz |
ASTM D150 | |
| Dielectric Strength | 17.0 kV/mm | 432 kV/in | ASTM D149 |
| Dissipation Factor | 0.0010 @Frequency 50.0 Hz |
0.0010 @Frequency 50.0 Hz |
ASTM D150 |
| 0.0020 @Frequency 1.00e+6 Hz |
0.0020 @Frequency 1.00e+6 Hz |
ASTM D150 | |
| Comparative Tracking Index | 250 V @Thickness 2.00 mm |
250 V @Thickness 0.0787 in |
Solution A; IEC 60112 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Average Extent of Burring | 3 cm | ASTM D635 |
Users viewing this material also viewed the following:
- PlastiComp Complet® LCF30-PPS Polyphenylene Sulfide, 30% Long Carbon Fiber Reinforced
- Haynes 230® alloy, 20% cold reduction, 1177°C anneal for 5 minutes
- SABIC Innovative Plastics LNP Lubricomp KCL36 Acetal Copoly
- ExxonMobil Enable™ 20-10CH Metallocene Polyethylene Resin (Africa & Middle East Grade)
- ACC EP WQS EPI Engineered Polymers Water Base Quick Set Epoxy
- Teknor Apex Sarlink® 4439D Thermoplastic Elastomer
- Fainplast Compounds PH 75/A Flexible PVC, Transparent Extrusion
- Rogers Corporation Bisco® EC-2040 Conductive Silicone
- Plenco 51015 PET, Pellet, Injection Molded, White (discontinued **)
Copyright © lookpolymers.com All Rights Reserved