ExxonMobil Bicor™ 25MB866 OPP Film

Category	Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Film Grade
Manufacturer	Exxon Chemical
Trade Name	Bicor™
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	ExxonMobil Bicor™ 25MB866 OPP Film.pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

Product Description: A high speed transparent, biaxially oriented polypropylene film, coated one side acrylic, one side PVOH. It provides excellent gas and aroma protection and is designed to be used as the outer web in modified atmosphere applications for dry products.Availability: Africa & Middle East, Asia Pacific and EuropeKey Features:Exceptional gas and aroma barrierOutstanding optical propertiesLow sealing threshold and broad sealing range on acrylic sideIdeal support for normal ink systemWater-based coatingsFeatures:Acrylic CoatedFlavor & Aroma BarrierGas BarrierIn Lamination Lap SealableOxygen BarrierPVOH CoatedApplications:BakeryBiscuits/Cookie/Crackers Crisps and SnacksDairy ProductsDry Foods and Beverage PowdersPet Food Uses:HFFS Flexible PackagingVFFS Flexible Packaging Processing Method: Cold Seal Adhesive, Inner Web Adhesive Lamination, Outer Web Adhesive Lamination, Solvent Flexographic Printing and Solvent Rotogravure PrintingInformation provided by ExxonMobil

Physical Properties	Metric	English	Comments
Water Vapor Transmission	1.10 g/m²/day @Temperature 23.0 °C	0.0710 g/100 in²/day @Temperature 73.4 °F	85% RH; ExxonMobil Method
	4.97 g/m²/day @Temperature 38.0 °C	0.320 g/100 in²/day @Temperature 100 °F	90% RH; ExxonMobil Method
Oxygen Transmission Rate	2.95 cc/m²/day @Temperature 23.0 °C	0.190 cc/100 in²/day @Temperature 73.4 °F	0% RH; ExxonMobil Method
Thickness	24.9 microns	0.980 mil	ExxonMobil Method
Coating Weight	22.1 g/m²	13.8 lb/ream	ExxonMobil Method

Mechanical Properties	Metric	English	Comments
Film Elongation at Break, MD	200 %	200 %	7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
Film Elongation at Break, TD	65 %	65 %	7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
Modulus of Elasticity	2.20 GPa	319 ksi	MD; ExxonMobil Method
	3.50 GPa	508 ksi	TD; ExxonMobil Method
Coefficient of Friction	0.25	0.25	Acrylic; ExxonMobil Method
Seal Strength	560 g/25 mm @Pressure 0.276 MPa, Temperature 130 °C	560 g/in @Pressure 40.0 psi, Temperature 266 °F	Otto Bruger, 0.2 sec; ExxonMobl Method
Film Tensile Strength at Break, MD	135 MPa	19600 psi	7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
Film Tensile Strength at Break, TD	275 MPa	39900 psi	7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method

Thermal Properties	Metric	English	Comments
Shrinkage, MD	5.0 % @Temperature 135 °C, Time 432 sec	5.0 % @Temperature 275 °F, Time 0.120 hour	ExxonMobil Method
Shrinkage, TD	5.0 % @Temperature 135 °C, Time 432 sec	5.0 % @Temperature 275 °F, Time 0.120 hour	ExxonMobil Method

Optical Properties	Metric	English	Comments
Haze	1.1 %	1.1 %	ExxonMobil Method
Gloss	90 %	90 %	45°; ExxonMobil Method

Descriptive Properties	Value	Comments
Carbon Dioxide Transmission Rate	5.16 cc/100 in²/ 24 hr	75% RH, ASTM D1434
Heat Seal Range	90°F	Acrylic Surface, 36.3 psi, 0.2 sec
Nitrogen Transmission Rate	0.645 cc/100 in²/ 24 hr	75% RH, ASTM D1434
Yield	31300 in²/lb