Styron CALIBREâ„¢ 203-22 Polycarbonate Resin
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | Styron |
| Trade Name | CALIBRE™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Styron CALIBREâ„¢ 203-22 Polycarbonate Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Overview: CALIBREâ„¢ 200-22 polycarbonate resins are produced in compliance with the US Food and Drug Administration (FDA) and EU food contact regulations. They provide excellent impact resistance, heat distortion resistance and optical clarity. The CALIBREâ„¢ 200-22 series products are available in 4 additive packages: CALIBREâ„¢ 200: No mold release or UV Stabilizer. CALIBREâ„¢ 201: Mold release. CALIBREâ„¢ 202: UV stabilizer. CALIBREâ„¢ 203: Mold release and UV stabilizer. (Note that CALIBREâ„¢ 202 and 203 grades are not available in Europe and do not comply with EU food contact regulations.) Applications:Food utensilsBeverages containersFood processor housings Other packaging applicationsGovt. and Industry Standards:US FDA 21 CFR 177.1580CSAUnderwriters Laboratory (UL)EU food contact 2002/72/ECInformation provided by Styron
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in³ | ISO 1183/A |
| Water Absorption | 0.32 % @Temperature 23.0 °C |
0.32 % @Temperature 73.4 °F |
Equilibrium, 50% RH; ISO 62 |
| 0.15 % @Temperature 23.0 °C, Time 86400 sec |
0.15 % @Temperature 73.4 °F, Time 24.0 hour |
ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | ISO 294-4 |
| Melt Flow | 22 g/10 min @Load 1.20 kg, Temperature 300 °C |
22 g/10 min @Load 2.65 lb, Temperature 572 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 72 | 72 | ASTM D785 |
| Hardness, Rockwell R | 118 | 118 | ASTM D785 |
| Tensile Strength at Break | 65.5 MPa | 9500 psi | 50 mm/min; ASTM D638 |
| 66.0 MPa | 9570 psi | ISO 527-2/50 | |
| Tensile Strength, Yield | 60.0 MPa | 8700 psi | 50 mm/min; ASTM D638; ISO 527-2/50 |
| Elongation at Break | 120 % | 120 % | 50 mm/min; ASTM D638 |
| Tensile Modulus | 2.30 GPa | 334 ksi | ISO 527-2/50 |
| 2.34 GPa | 339 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 96.5 MPa | 14000 psi | Method I (3 point load), 2.0 mm/min; ASTM D790 |
| 97.0 MPa | 14100 psi | 2.0 mm/min; ISO 178 | |
| Flexural Modulus | 2.40 GPa | 348 ksi | 2.0 mm/min; ISO 178 |
| 2.41 GPa | 350 ksi | Method I (3 point load), 2.0 mm/min; ASTM D790 | |
| Izod Impact, Notched | 7.50 J/cm @Temperature 23.0 °C |
14.1 ft-lb/in @Temperature 73.4 °F |
ASTM D256 |
| Izod Impact, Notched (ISO) | 74.0 kJ/m² @Temperature 23.0 °C |
35.2 ft-lb/in² @Temperature 73.4 °F |
ISO 180/4A |
| Izod Impact, Unnotched (ISO) | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ISO 180; ASTM D256A |
| Tensile Impact Strength | 378 kJ/m² | 180 ft-lb/in² | ASTM D1822 |
| Dart Drop, Total Energy | 72.3 J | 53.3 ft-lb | 3.39 m/sec; ASTM D3763 |
| Abrasion | 45 | 45 | [%] Taber; ASTM D1004 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 68.0 µm/m-°C @Temperature -40.0 - 82.0 °C |
37.8 µin/in-°F @Temperature -40.0 - 180 °F |
ASTM D696 |
| Hot Ball Pressure Test | 125 °C | 257 °F | IEC 60335-1 |
| Deflection Temperature at 0.46 MPa (66 psi) | 139 °C | 282 °F | Annealed; ISO 75-2/B; ASTM D648 |
| 142 °C | 288 °F | Unannealed; ISO 75-2/B | |
| Deflection Temperature at 1.8 MPa (264 psi) | 126 °C | 259 °F | Unannealed; ASTM D648 |
| 126 °C | 259 °F | Annealed; ISO 75-2/A | |
| 136 °C | 277 °F | Annealed; ASTM D648 | |
| Vicat Softening Point | 147 °C @Load 5.10 kg |
297 °F @Load 11.2 lb |
Rate A (50°C/h); ASTM D1525; ISO 360/B50 |
| Flammability, UL94 | HB @Thickness 1.59 mm |
HB @Thickness 0.0626 in |
|
| HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
||
| Oxygen Index | 26 % | 26 % | ISO 4289-2 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Refractive Index | 1.586 | 1.586 | ASTM D542; ISO 489 |
| Haze | 1.0 % | 1.0 % | ASTM D1003 |
| Transmission, Visible | 89 % | 89 % | ASTM D1003 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 2.00e+17 ohm-cm | 2.00e+17 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.0 @Frequency 60.0 Hz |
3.0 @Frequency 60.0 Hz |
ASTM D150 |
| 3.0 @Frequency 1.00e+6 Hz |
3.0 @Frequency 1.00e+6 Hz |
ASTM D150 | |
| Dielectric Strength | 17.0 kV/mm | 432 kV/in | ASTM D149 |
| Dissipation Factor | 0.0010 @Frequency 50.0 Hz |
0.0010 @Frequency 50.0 Hz |
ASTM D150 |
| 0.0020 @Frequency 1.00e+6 Hz |
0.0020 @Frequency 1.00e+6 Hz |
ASTM D150 | |
| Comparative Tracking Index | 250 V @Thickness 2.00 mm |
250 V @Thickness 0.0787 in |
Solution A; IEC 60112 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Average Extent of Burring | 3 cm | ASTM D635 |
Users viewing this material also viewed the following:
- Northstar Polymers PNA-157 Curing Agent
- Lucas-Milhaupt Silvacore® A50N Flux Cored Brazing Alloy
- SABIC Innovative Plastics LNP THERMOCOMP PFW64 PA 6
- SABIC Innovative Plastics LNP THERMOCOMP MF006SU PP
- Borealis BorPEX™ HE2556 Black High Density Polyethylene Powder for Crosslinked Pipes
- A. Schulman POLYBATCH™ AO-25 Antioxidant Masterbatch Based in LDPE
- 3M 1614 Polyester Protective Tape
- Azdel Plus R301B01N 30% Continuous Random Fiber Mat / PP Resin Matrix
- 3M 766 Hazard Marking Vinyl Tape
- Teknor Apex Sinpolene TPP1030 Polypropylene
Copyright © lookpolymers.com All Rights Reserved