Styron CALIBREâ„¢ 200-6 Polycarbonate Resin
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | Styron |
| Trade Name | CALIBRE™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Styron CALIBREâ„¢ 200-6 Polycarbonate Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Overview: CALIBREâ„¢ 200-6 polycarbonate resins are produced in compliance with the US Food and Drug Administration (FDA) and EU food contact regulations. They provide excellent impact resistance, heat distortion resistance and optical clarity as well as high melt strength for sheet extrusion applications. The CALIBREâ„¢ 200-6 series products are available in 4 additive packages: CALIBREâ„¢ 200: No mold release or UV Stabilizer. CALIBREâ„¢ 201: Mold release. CALIBREâ„¢ 202: UV stabilizer. CALIBREâ„¢ 203: Mold release and UV stabilizer. (Note that CALIBRE 202 and 203 grades are not available in Europe and do not comply with EU food contact regulations)Applications:Food and processor housingsBeverage containers/service wareSmall & large appliancesLiquid containersCustom sheetPackaging applicationsGovt. and Industry Standards:US FDA 21 CFR 177.1580Underwriters Laboratory (UL)CSAEU food contact 2002/72/ECInformation provided by Styron
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in³ | ISO 1183/A; ASTM D792 |
| Water Absorption | 0.32 % @Temperature 23.0 °C |
0.32 % @Temperature 73.4 °F |
Equilibrium, 50% RH; ISO 62; ASTM D570 |
| 0.15 % @Temperature 23.0 °C, Time 86400 sec |
0.15 % @Temperature 73.4 °F, Time 24.0 hour |
ISO 62; ASTM D570 | |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | ISO 294-4; ASTM D955 |
| Melt Flow | 6.0 g/10 min @Load 1.20 kg, Temperature 300 °C |
6.0 g/10 min @Load 2.65 lb, Temperature 572 °F |
ISO 1133; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 73 | 73 | ASTM D785 |
| Hardness, Rockwell R | 118 | 118 | ASTM D785 |
| Tensile Strength at Break | 72.0 MPa | 10400 psi | ISO 527-2/50 |
| 72.4 MPa | 10500 psi | 50 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 60.0 MPa | 8700 psi | 50 mm/min; ASTM D638 |
| Elongation at Break | 150 % | 150 % | 50 mm/min; ASTM D638 |
| Elongation at Yield | 6.0 % | 6.0 % | 50 mm/min; ASTM D638; ISO 527-2/50 |
| Tensile Modulus | 2.30 GPa | 334 ksi | ISO 527-2/50 |
| 2.41 GPa | 350 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 96.5 MPa | 14000 psi | Method I (3 point load), 2.0 mm/min; ASTM D790 |
| 97.0 MPa | 14100 psi | 2.0 mm/min; ISO 178 | |
| Flexural Modulus | 2.40 GPa | 348 ksi | 2.0 mm/min; ISO 178 |
| 2.41 GPa | 350 ksi | Method I (3 point load), 2.0 mm/min; ASTM D790 | |
| Izod Impact, Notched | 9.10 J/cm @Temperature 23.0 °C |
17.0 ft-lb/in @Temperature 73.4 °F |
ASTM D256 |
| Izod Impact, Notched (ISO) | 93.0 kJ/m² @Temperature 23.0 °C |
44.3 ft-lb/in² @Temperature 73.4 °F |
ISO 180/A |
| Izod Impact, Unnotched (ISO) | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ISO 180 |
| Tensile Impact Strength | 588 kJ/m² | 280 ft-lb/in² | ASTM D1822 |
| Dart Drop, Total Energy | 90.4 J | 66.7 ft-lb | 3.39 m/sec; ASTM D3763 |
| Abrasion | 45 | 45 | [%] Taber; ASTM D1004 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 68.0 µm/m-°C @Temperature -40.0 - 82.0 °C |
37.8 µin/in-°F @Temperature -40.0 - 180 °F |
ASTM D696 |
| Hot Ball Pressure Test | 125 °C | 257 °F | IEC 60335-1 |
| Deflection Temperature at 0.46 MPa (66 psi) | 145 °C | 293 °F | Annealed; ASTM D648 |
| 146 °C | 295 °F | Annealed; ISO 75-2/B | |
| Deflection Temperature at 1.8 MPa (264 psi) | 126 °C | 259 °F | Annealed; ISO 75-2/A |
| 129 °C | 264 °F | Unannealed; ASTM D648 | |
| 142 °C | 288 °F | Unannealed; ASTM D648 | |
| 143 °C | 289 °F | Annealed; ISO 75-2/A | |
| Vicat Softening Point | 151 °C @Load 5.10 kg |
304 °F @Load 11.2 lb |
Rate A (50°C/h); ASTM D1525; ISO 360/B50 |
| Flammability, UL94 | HB @Thickness 1.59 mm |
HB @Thickness 0.0626 in |
|
| HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Refractive Index | 1.586 | 1.586 | ASTM D542; ISO 489 |
| Haze | 1.0 % | 1.0 % | ASTM D1003 |
| Transmission, Visible | 89 % | 89 % | ASTM D1003 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 2.00e+17 ohm-cm | 2.00e+17 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.0 @Frequency 60.0 Hz |
3.0 @Frequency 60.0 Hz |
ASTM D150 |
| 3.0 @Frequency 1.00e+6 Hz |
3.0 @Frequency 1.00e+6 Hz |
ASTM D150 | |
| Dielectric Strength | 17.0 kV/mm | 432 kV/in | ASTM D149 |
| Dissipation Factor | 0.0010 @Frequency 50.0 Hz |
0.0010 @Frequency 50.0 Hz |
ASTM D150 |
| 0.0020 @Frequency 1.00e+6 Hz |
0.0020 @Frequency 1.00e+6 Hz |
ASTM D150 | |
| Comparative Tracking Index | 250 V @Thickness 2.00 mm |
250 V @Thickness 0.0787 in |
Solution A; IEC 60112 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Average Extent of Burring | 3 cm | ASTM D635 |
Users viewing this material also viewed the following:
- Chevron Phillips Marlex® C590 High Density Polyethylene (discontinued **)
- Overview of materials for Polycarbonate, Impact Modified
- Indium Corp. #1010 Wave Solder Flux, Water-Soluble
- Karina 651-48/1-B-IS-BZ Black PVC Compound
- Tisan TISLAMID® 6 30% Glass Filled Impact Modified Nylon 6
- EMS-Grivory Grivory® XE 4104 black 9992 PA610-GF40
- Denka VINYKON W4200 PVC, W grade for equipment cords, for heat resistance
- DuPont Teijin Films Mylar® OB01 Polyester Packaging Film, 50 Gauge
- Alliance Polymers Zythane™ 3045D Thermoplastic Polyurethane Elastomer
Copyright © lookpolymers.com All Rights Reserved