Plastcom PLASTALEN® PQ 82 N Polypropylene with improved impact strength

Category	Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Impact Modified; Molded/Extruded
Manufacturer	Plastcom spol. s r.o.
Trade Name	PLASTALEN®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Plastcom PLASTALEN® PQ 82 N Polypropylene with improved impact strength.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

PP impact modified. General application in all industry branches. Delivered in natural mode and in the full RAL color scale. For injection molding.Information Provided by Plastcom spol. s r.o.

Physical Properties	Metric	English	Comments
Density	0.940 g/cc	0.0340 lb/in³	STN EN ISO 1183-1
Linear Mold Shrinkage	0.013 cm/cm	0.013 in/in	STN EN ISO 294-4
Linear Mold Shrinkage, Transverse	0.015 cm/cm	0.015 in/in	STN EN ISO 294-4
Melt Flow	20 g/10 min @Load 2.16 kg, Temperature 230 °C	20 g/10 min @Load 4.76 lb, Temperature 446 °F	STN EN ISO 1133

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	23.0 MPa	3340 psi	STN EN ISO 527-2
Elongation at Break	50 %	50 %	STN EN ISO 527-2
Tensile Modulus	1.50 GPa	218 ksi	STN EN ISO 527-2
Flexural Strength	17.0 MPa	2470 psi	STN EN ISO 178
Flexural Modulus	1.05 GPa	152 ksi	STN EN ISO 178
Charpy Impact Unnotched	NB @Temperature 23.0 °C	NB @Temperature 73.4 °F	STN EN ISO 179
	NB @Temperature -20.0 °C	NB @Temperature -4.00 °F	STN EN ISO 179
Charpy Impact, Notched	0.350 J/cm² @Temperature -20.0 °C	1.67 ft-lb/in² @Temperature -4.00 °F	STN EN ISO 179
	1.00 J/cm² @Temperature 23.0 °C	4.76 ft-lb/in² @Temperature 73.4 °F	STN EN ISO 179

Thermal Properties	Metric	English	Comments
Melting Point	160 °C	320 °F	STN EN 11357-1
Deflection Temperature at 1.8 MPa (264 psi)	65.0 °C	149 °F	STN EN ISO 75-2 (A)
Vicat Softening Point	115 °C	239 °F	STN EN ISO 306
Flammability, UL94	HB	HB

Processing Properties	Metric	English	Comments
Melt Temperature	200 - 250 °C	392 - 482 °F
Mold Temperature	40.0 - 70.0 °C	104 - 158 °F
Drying Temperature	80.0 °C @Time 14400 sec	176 °F @Time 4.00 hour
Moisture Content	0.10 %	0.10 %	STN EN ISO 3344
Injection Pressure	70.0 - 120 MPa	10200 - 17400 psi