Styrolution PS 454N HIPS
| Category | Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Impact Modified |
| Manufacturer | Styrolution |
| Trade Name | PS |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Styrolution PS 454N HIPS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Styrolution PS 454N is an impact resistant polystyrene with a good balance of toughness, high flow, heat resistance and high gloss.Good balance of toughness, high flow, and heat resistanceHigh glossUL 94 HBInformation provided by Styrolution
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | <= 0.10 % @Temperature 23.0 °C |
<= 0.10 % @Temperature 73.4 °F |
50% RH; ISO 62 |
| Water Absorption at Saturation | <= 0.10 % @Temperature 23.0 °C |
<= 0.10 % @Temperature 73.4 °F |
ISO 62 |
| Linear Mold Shrinkage | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in | ISO 294-4 |
| Melt Flow | 14 g/10 min @Load 5.00 kg, Temperature 200 °C |
14 g/10 min @Load 11.0 lb, Temperature 392 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 90.0 MPa | 13100 psi | ISO 2039-1 |
| Tensile Strength, Yield | 27.0 MPa | 3920 psi | ISO 527 |
| Elongation at Break | 25 % | 25 % | ISO 527 |
| Elongation at Yield | 1.4 % | 1.4 % | ISO 527 |
| Tensile Modulus | 2.20 GPa | 319 ksi | ISO 527 |
| Flexural Strength | 41.0 MPa | 5950 psi | ISO 178 |
| Flexural Modulus | 2.30 GPa | 334 ksi | ISO 178 |
| Charpy Impact Unnotched | 1.60 J/cm² | 7.61 ft-lb/in² | ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 80.0 µm/m-°C | 44.4 µin/in-°F | ISO 11359 |
| Thermal Conductivity | 0.170 W/m-K | 1.18 BTU-in/hr-ft²-°F | DIN 52612-1 |
| Deflection Temperature at 0.46 MPa (66 psi) | 82.0 °C | 180 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 78.0 °C | 172 °F | ISO 75 |
| Vicat Softening Point | 82.0 °C @Load 5.10 kg |
180 °F @Load 11.2 lb |
120°C/h; ASTM D 1525 |
| 91.0 °C @Load 1.02 kg |
196 °F @Load 2.25 lb |
50°C/h; ISO 306 | |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+18 ohm-cm | >= 1.00e+18 ohm-cm | IEC 60093 |
| Surface Resistance | >= 1.00e+13 ohm | >= 1.00e+13 ohm | IEC 60093 |
| Dielectric Constant | 2.5 @Frequency 100 Hz |
2.5 @Frequency 100 Hz |
IEC 60250 |
| Dissipation Factor | 0.00015 @Frequency 100 Hz |
0.00015 @Frequency 100 Hz |
IEC 60250 |
| 0.00040 @Frequency 1.00e+6 Hz |
0.00040 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 180 - 260 °C | 356 - 500 °F | ISO 294 |
| Mold Temperature | 40.0 °C | 104 °F | ISO 294 |
| Injection Velocity | 200 mm/sec | 7.87 in/sec | ISO 294 |
Users viewing this material also viewed the following:
- Polimeri Europa Riblene® FF 20 Low Density Polyethylene - Blown Film Extrusion
- NOVA Chemicals Novapol® TR-0242-U MDPE Rotational Molding Resin (discontinued **)
- Kennametal Stellite Nucalloy® 41 Nickel-Chromium-Boron Alloy
- H.C. Starck 4201 Pure Tungsten WF-3, Foil
- Schwartz Technical Plastics LAMIGAMID® 317 Cast Polyamide 6, Heat Stabilized, Conditioned
- Stir SpA IN 3500 AF CZ (PVC)
- Techmer ES Plaslube® J-1/30/TF/15 NAT PA66
- ExxonMobil Escorene™ UL 15028EM1 Ethylene Vinyl Acetate Copolymer (European Grade)
- ExxonMobil Escorene™ AD 2528EH2 Ethylene Vinyl Acetate Copolymer (European Grade)
- Loctite® Durabond® E-00CL Epoxy Adhesive
Copyright © lookpolymers.com All Rights Reserved